Melt Flow Property of Fiber Reinforced Nylon and Polycarbonate
نویسندگان
چکیده
منابع مشابه
Melt volume flow rate and melt flow rate of kenaf fibre reinforced Floreon/magnesium hydroxide biocomposites
A study of the melt volume flow rate (MVR) and the melt flow rate (MFR) of kenaf fibre (KF) reinforced Floreon (FLO) and magnesium hydroxide (MH) biocomposites under different temperatures (160-180 °C) and weight loadings (2.16, 5, 10 kg) is presented in this paper. FLO has the lowest values of MFR and MVR. The increment of the melt flow properties (MVR and MFR) has been found for KF or MH inse...
متن کاملMechanical Property Evaluation of Fiber-Reinforced and Fabric-Reinforced Zinc Oxide-Eugenol Temporary Filling Materials
Zinc oxide-eugenol (ZOE) is usually applied clinically as dental filling material for thermal insulation and temporary restoration. The objective of this study was to use ZOE as a composite matrix and low melting-point polyester fibers or fabrics as reinforcement. The added fibers or fabrics increased the composite materials’ compressive load by 250 N and 290 N, respectively. Fiber length and t...
متن کاملmechanical and morphological properties of short nylon fiber reinforced acrylonitrile-butadiene rubber composites
acrylonitrile butadiene rubber (nbr) composites are prepared from waste nylon 66 short fiber using a two-roll mill mixer. the effects of fiber content and bonding agent on the mechanical and morphological properties of the composites are studied. the curing characteristics of the composites have been studied by using cure rheometer. the cure and scorch time of the composites decrease while cure...
متن کاملEnhancement of interfacial properties of basalt fiber reinforced nylon 6 matrix composites with silane coupling agents
In this work solution surface treatment was applied for producing basalt fiber reinforced PA6 matrix composites. Beyond scanning electron microscopy, static and dynamic mechanical tests, dynamic mechanical analysis of composites was used for qualifying the interfacial adhesion in a wide temperature range. The loss factor peak height of loss factor is particularly important, because it is in clo...
متن کاملMorphology and Melt Rheology of Nylon 11/Clay Nanocomposites
Nylon 11 (PA11)/clay nanocomposites have been prepared by melt-blending, followed by melt-extrusion through a capillary. Transmission electron microscopy shows that the exfoliated clay morphology is dominant for low nanofiller content, while the intercalated one is prevailing for high filler loading. Melt rheological properties of PA11 nanocomposites have been studied in both linear and nonline...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Sen'i Kikai Gakkaishi (Journal of the Textile Machinery Society of Japan)
سال: 1988
ISSN: 0371-0580,1880-1994
DOI: 10.4188/transjtmsj.41.3_t39