Mechanochemical synthesis of bismuth ferrite
نویسندگان
چکیده
منابع مشابه
Synthesis and characterization of Lanthanum doped Bismuth Ferrite
B1-xLaxFeO3 (x = 0.0, 0.025) crystallites were prepared by chemical solution route. XRD analysis confirmed the phase formation of the materials. Thermal characterization was done by DSC-TGA to confirm crystallization and thermal behavior for phase development. Morphological studies by FESEM showed the agglomerated nature of the ferrite...
متن کاملSynthesis and characterization of Lanthanum doped Bismuth Ferrite
B1-xLaxFeO3 (x = 0.0, 0.025) crystallites were prepared by chemical solution route. XRD analysis confirmed the phase formation of the materials. Thermal characterization was done by DSC-TGA to confirm crystallization and thermal behavior for phase development. Morphological studies by FESEM showed the agglomerated nature of the ferrite...
متن کاملMechanochemical Synthesis and Characterisation of Bismuth-Niobium Oxide Ion Conductors
Bismuth niobate solid solutions, BixNbOδ (2.5 ≤ x ≤ 6), have been prepared using a mechanochemical method. The solid solutions were also prepared using a solidstate conventional method for comparison purposes. Bi3NbO7 was successfully obtained via a mechanochemical method at a lower synthesis temperature (milled at 1000 rpm for one hour followed by heating at 700C for 24 h) than the conventiona...
متن کاملsynthesis and characterization of lanthanum doped bismuth ferrite
b1-xlaxfeo3 (x = 0.0, 0.025) crystallites were prepared by chemical solution route. xrd analysis confirmed the phase formation of the materials. thermal characterization was done by dsc-tga to confirm crystallization and thermal behavior for phase development. morphological studies by fesem showed the agglomerated nature of the ferrite and edx analysis confirmed the degree of doping. ftir studi...
متن کاملMechanochemical synthesis of alumina nanoparticles
Abstract: Nano- size alumina particles have been synthesized by mechanical activation of a dry powder mixture of AlCl3 and CaO. Mechanical milling of the above raw materials with the conditions adopted in this study resulted in the formation of a mixture consisting of crystalline CaO and amorphous aluminum chlorides phases. There was no sign of chemical reaction occurring during milling stag...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Mining and Metallurgy, Section B: Metallurgy
سال: 2013
ISSN: 1450-5339,2217-7175
DOI: 10.2298/jmmb120430039m