Mechanochemical synthesis and ionic conductivity of lanthanum phosphosilicate oxyapatites
نویسندگان
چکیده
منابع مشابه
Lanthanum Telluride: Mechanochemical Synthesis of a Refractory Thermoelectric Material
Recent experimental work on lanthanum telluride has confirmed its significant potential as an n-type material for high temperature thermoelectric (TE) power generation application. The phase of interest, La3.xTe4, has a Th3P4 defect structure where x is the lanthanum vacancy with values ranging between 0 and 1/3. Thermoelectric properties change rapidly with x since the carrier concentration, «...
متن کاملsingle-step synthesis of multi-component spirobarbiturates using ionic liquids and synthesis of substituted pyridine filled with catalysts supported on solid substrate
in this thesis, a better reaction conditions for the synthesis of spirobarbiturates catalyzed by task-specific ionic liquid (2-hydroxy-n-(2-hydroxyethyl)-n,n-dimethylethanaminium formate), calcium hypochlorite ca(ocl)2 or n-bromosuccinimide (nbs) in the presence of water at room temperature by ultrasonic technique is provided. the design and synthesis of spirocycles is a challenging task becaus...
15 صفحه اولMechanochemical synthesis and high temperature thermoelectric properties of calcium-doped lanthanum telluride La3xCaxTe4
The thermoelectric properties from 300–1275 K of calcium-doped La3 xTe4 are reported. La3 xTe4 is a high temperature n-type thermoelectric material with a previously reported zTmax B 1.1 at 1273 K and x = 0.23. Computational modeling suggests the La atoms define the density of states of the conduction band for La3 xTe4. Doping with Ca 2+ on the La site is explored as a means of modifying the de...
متن کاملMechanochemical synthesis of alumina nanoparticles
Abstract: Nano- size alumina particles have been synthesized by mechanical activation of a dry powder mixture of AlCl3 and CaO. Mechanical milling of the above raw materials with the conditions adopted in this study resulted in the formation of a mixture consisting of crystalline CaO and amorphous aluminum chlorides phases. There was no sign of chemical reaction occurring during milling stag...
متن کاملAg13I4(AsO4)3: Synthesis, Crystal Structure and Ionic Conductivity
Ruby-red single crystals of Ag13I4(AsO4)3 were prepared for the first time by reacting a stoichiometric mixture of Ag2O, AgI and As2O3 at elevated oxygen pressure of 120 MPa and at a temperature of 350 ◦C. The polyhedral crystals belong to the monoclinic space group P21/m with a = 9.247(1), b = 7.152(1), c = 17.674(2) Å, β = 91.492(2)◦, and Z = 2. The structure is fully ordered and was solved b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Comptes Rendus Chimie
سال: 2014
ISSN: 1631-0748
DOI: 10.1016/j.crci.2013.10.018