Mechanism of Erosion-Corrosion on Copper Alloys
نویسندگان
چکیده
منابع مشابه
Study of Copper Bearing Alloys Corrosion Characteristics
This paper addresses investigation of the corrosion behavior of copper bearing anodes with high nickel content. Anodes are produced from different solid wastes formed during the copper or nickel row materials treatment. Nickel content in anode samples had values up to 10 mas %. The content of tin, lead and antimony was up to 1 % for each of elements. Sulphuric acid solution, concentration of 17...
متن کاملCorrosion mechanism of Ti-Cr alloys in solution containing fluoride.
OBJECTIVE The objective of this study was to clarify the influence of chromium content on surface reaction of Ti-Cr alloys in an acidic fluoride-containing saline solution. METHODS Four Ti-Cr alloys containing 5, 10, 15 or 20 mass% chromium were characterized in terms of dissolution of metals in an acidic fluoride-containing saline solution and surface structure by X-ray photoelectron spectro...
متن کاملCorrosion Mechanism of Al-zn-in Alloys in Chloride Solutions
The electrochemical behavior of Al-ZnIn alloys was investigated in chloride media by means of potentiodynamic techniques, complemented by Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Analysis (EDX) and Transmission Electron Microscopy (TEM). The influence of local alkalization produced by previous cathodization was analyzed at potentials more negative than the rest potential. The...
متن کاملPolystyrene films as barrier layers for corrosion protection of copper and copper alloys.
Dip-coated polystyrene layers of sub-micrometre thickness (85-500nm) have been applied on copper and copper alloys (aluminium brass, copper-nickel 70/30), as well as on stainless steel 304, and produced an effective barrier against corrosion and adhesion of corrosion-relevant microorganisms. According to the dynamic wettability measurements, the coatings exhibited high advancing (103°), recedin...
متن کاملErosion-corrosion and wear
The basic processes of wear, erosion and erosion-corrosion are reviewed. It is shown that oxide debris can accelerate wear when it is present as particulates, or protect and reduce friction when it is present as a glaze. Erosion-corrosion processes can be understood and organized in a series of regimes that represent a sequence of change in the relative intensities of erosive and corrosive proc...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: CORROSION ENGINEERING
سال: 1986
ISSN: 0010-9355,1884-1155
DOI: 10.3323/jcorr1974.35.12_706