MECHANICAL PROPERTIES OF WOOD PLASTIC COMPOSITES WITH THE ACTIVATED WOOD FILLER
نویسندگان
چکیده
The aim of the research was a study effect activation birch sawdust microparticles with dilute solution sodium hydroxide at low temperature on mechanical properties and water sorption obtained wood plastic composite (WPC) samples from by-product domestic processing recycled polymer municipal waste. It found that (tensile, bending) WPC filled activated were higher than those initial sawdust. swelling degree filler lower for However, difference in values relatively comparison observed essential their properties. This fact explained by enhanced content carbonyl groups are able to absorb water.
منابع مشابه
Some of the Properties of Wood Plastic Composites
In this study some of the important properties of experimentally manufactured wood– plastic composites (WPC) were determined. Specimen having 60% and 80% particle and fibre of radiata pine (Pinus radiata ) were mixed with polypropylene (plastic) and four different additives, namely Struktol TR 016 which is coupling agent, CIBA antimicrobial agent (IRGAGUARD F3510) as fungicide, CIBA UV filter c...
متن کاملeffect of blending method on the mechanical properties of wood-plastic composites
in this study, the possibility of producing wood-plastic panels was studied using two different blending methods including melt blend and dry blend. wood-plastic panels were made from recycled high density polyethylene (as resin) and mdf waste (as natural fiber) at 60, 70 and 80% by weight filler loading. nominal density and dimensions of the panels were 1g/cm3 and 35×35×1 cm, respectively. the...
متن کاملProperties of Flat-Pressed Wood Plastic Composites Containing Fire Retardants
This study investigated physical, mechanical, and fire properties of the flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (FRs) [5 or 15% by weight (wt)] at 50 wt % of the wood flour (WF). The WPC panels were made from dryblended WF, polypropylene (PP) with maleic anhydridegrafted PP (2 wt %), and FR powder formulations using a conventional flat-pressing pro...
متن کاملFlat-pressed wood plastic composites from sawdust and recycled polyethylene terephthalate (PET): physical and mechanical properties
This study deals with the fabrication of composite matrix from saw dust (SD) and recycled polyethylene terephthalate (PET) at different ratio (w/w) by flat-pressed method. The wood plastic composites (WPCs) were made with a thickness of 6 mm after mixing the saw dust and PET in a rotary type blender followed by flat press process. Physical i.e., density, moisture content (MC), water absorption ...
متن کاملDynamic Mechanical Analysis of Compatibilizer Effect on the Mechanical Properties of Wood Flour-High-Density Polyethylene Composites
In this study, effect of MAPE (maleic anhydride polyethylene) as the compatibilizer on the mechanical properties of wood-flour polyethylene composites has been investigated by using Dynamic Mechanical Analysis (DMA). Composites were made at 25% and 50% by weight fiber contents and 1% and 2% compatibilizer respectively. Controls were also made at the same fiber contents without the compatibilize...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Vide. Tehnolo?ija. Resursi
سال: 2021
ISSN: ['2256-070X', '1691-5402']
DOI: https://doi.org/10.17770/etr2021vol1.6584