Mechanical behaviour of pack carburized AISI 316L austenitic stainless steel
نویسندگان
چکیده
منابع مشابه
Haemocompatibility of Surface Modified AISI 316L Austenitic Stainless Steel Tested in Artificial Plasma
The study comprises evaluation of suitability of passive layer created on the surface of AISI 316L stainless steel for products that are intended to have contact with blood. For that purpose, prior to and after chemical passivation, samples were subject to 7 day exposure in artificial plasma at the temperature of T=37°C. Next, tests of metallic ions infiltration from the surface to the solution...
متن کاملBiomaterial Studies on AISI 316L Stainless Steel after Magnetoelectropolishing
The polarisation characteristics of the electropolishing process in a magnetic field (MEP – magnetoelectropolishing), in comparison with those obtained under standard/conventional process (EP) conditions, have been obtained. The occurrence of an EP plateau has been observed in view of the optimization of MEP process. Up-to-date stainless steel surface studies always indicated some amount of fre...
متن کاملMicro abrasion-corrosion of AISI 316L stainless steel
In this study, the synergistic effects of abrasion and corrosion on AISI 316L stainless steel have been investigated using a micro-abrasion test rig. A series of results from abrasioncorrosion tests conducted using the micro-abrasion rig are presented. AISI 316L stainless steel has been studied under both pure abrasion and abrasion-corrosion conditions simulated by either distilled water or 3.5...
متن کاملFatigue behavior of Austenitic Type 316L Stainless Steel
The aim of this work is to determine the fatigue life of 316L stainless steel. The mechanisms of fatigue of 316L stainless steels were investigated and discussed. The fatigue tests were carried out at constant-amplitude cyclic loading with load ratio R=0.1. Scanning Electron Microscope (SEM) is then used to examine the fracture surface. The results show that the fatigue limit of 316L stainless ...
متن کاملDetermination of susceptibility to intergranular corrosion and electrochemical reactivation behaviour of AISI 316L type stainless steel
In this study, double loop electrochemical potentiokinetic reactivation (DLEPR) test was applied to determine the degree of sensitization in 316L type stainless steel, where obtained results were correlated with revealed microstructures after oxalic acid test and weight loss measurements of Streicher and Huey acid tests. Best agreement was provided with test parameters which are 1 M H2SO4 and 0...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Southern African Institute of Mining and Metallurgy
سال: 2015
ISSN: 2411-9717
DOI: 10.17159/2411-9717/2015/v115n12a6