Material Property Evaluation of Heat-treated CF/PA 6 Woven Fabric Laminates Formed by <i>in-situ</i> Polymerization

نویسندگان

چکیده

In this study, carbon fiber (CF)/polyamide 6 (PA 6) fabric laminates molded by in-situ polymerization using ε-caprolactam were evaluated. To investigate the effect of CF sizing agent on their molecular weight distributions PA in CF/PA and mechanical properties, we removed a surface heat treatment before molding. The concentrations monomer oligomer (carbon reinforced thermoplastics (CFRTP)) applied with pretreatment lower than those having no pretreatment. weights matrix resin CFRTPs which was higher Bending strength tensile Those results indicate properties CFRTP. A is an effective method for decreasing unreacted components increasing strength.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

investigation of thermal comfort properties of woven sport fabric using blend of estabragh fibers

امروزه لباس در نظر ورزشکاران و کسانی که برای اوقات فراغت خود و یا برای رسیدن به اندامی متعادل، ورزش می کنند؛ بسیار با اهمیت است. احساس مطلوب از لباس در زمره خصوصیات راحتی پوشش می باشد. خصوصیات انتقال رطوبت لباس، در ارزیابی راحتی حسی و حرارتی منسوجات تولید شده از آن ها بسیار مهم است. هدف از این تحقیق، معرفی پارچه جدید است که متشکل از الیاف استبرق با خواص منحصر به فرد می باشد. استبرق لیف طبیعی تو...

Thermomechanical Properties of Woven Fabric Composites

The in-plane thermo-elastic behaviour of woven fabric reinforced composites is analysed using a combination of published micromechanics and finite element techniques. The repetitive unit of an arbitrary woven fabric composite is divided into elements of which the thermo-elastic properties are determined using micromechanics. The properties of the repetitive unit are obtained using the finite el...

متن کامل

Impact Damage in Woven Fabric Reinforced Composites

INTRODUCTION Very often, woven fabrics are used as the reinforcement in advanced composite materials. Although the resulting inplane stiffness is lower than of their unidirectional counterparts, the excellent drapability of these materials eases the production of more general doubly curved components. In addition, the inherently low out-of-plane strength of these layered materials improves due ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Seikei kakou

سال: 2023

ISSN: ['0915-4027', '1883-7417']

DOI: https://doi.org/10.4325/seikeikakou.35.281