Magnetization enhancement in magnetite nanoparticles capped with alginic acid
نویسندگان
چکیده
منابع مشابه
Synthesis of stabilized myrrh-capped hydrocolloidal magnetite nanoparticles.
Herein we report a new method for synthesizing stabilized magnetic nanoparticle (MNP) colloids. A new class of monodisperse water-soluble magnetite nano-particles was prepared by a simple and inexpensive co-precipitation method. Iron ions and iodine were prepared by the reaction between ferric chloride and potassium iodide. The ferrous and ferric ions were hydrolyzed at low temperature at pH 9 ...
متن کاملAlginic Acid-Coated Chitosan Nanoparticles Loaded with Legumain DNA Vaccine: Effect against Breast Cancer in Mice
Legumain-based DNA vaccines have potential to protect against breast cancer. However, the lack of a safe and efficient oral delivery system restricts its clinical application. Here, we constructed alginic acid-coated chitosan nanoparticles (A.C.NPs) as an oral delivery carrier for a legumain DNA vaccine. First, we tested its characteristic in acidic environments in vitro. DNA agarose electropho...
متن کاملHigh-Temperature Magnetism as a Probe for Structural and Compositional Uniformity in Ligand-Capped Magnetite Nanoparticles
To investigate magnetostructural relationships in colloidal magnetite (Fe3O4) nanoparticles (NPs) at high temperature (300-900 K), we measured the temperature dependence of magnetization (M) of oleate-capped magnetite NPs ca. 20 nm in size. Magnetometry revealed an unusual irreversible high-temperature dependence of M for these NPs, with dip and loop features observed during heating-cooling cyc...
متن کاملIonomeric Films of Alginic Acid
Transparent, flexible films could be made by casting aqueous solutions of alginic acid, but they dissolved in water. When films were made from a solution of alginic acid and multivalent ions, they were still water soluble. However, when alginic acid films were immersed in a solution of salts with multivalent ions, they dissolved in water much more slowly, if at all. Treatment with calcium and z...
متن کاملOrigin of reduced magnetization and domain formation in small magnetite nanoparticles
The structural, chemical, and magnetic properties of magnetite nanoparticles are compared. Aberration corrected scanning transmission electron microscopy reveals the prevalence of antiphase boundaries in nanoparticles that have significantly reduced magnetization, relative to the bulk. Atomistic magnetic modelling of nanoparticles with and without these defects reveals the origin of the reduced...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Composites Part B: Engineering
سال: 2014
ISSN: 1359-8368
DOI: 10.1016/j.compositesb.2014.04.022