Magnetic properties of iron films on anodized aluminum underlayer
نویسندگان
چکیده
منابع مشابه
Magnetic properties and underlayer thickness in SmCoÕCr films
SmCo films with a Cr underlayer have been investigated as potentially attractive candidates for high density recording media. Magnetron sputtering was used here to produce Cr/SmCox /Cr films on Si ~100! substrates. The magnetic films were deposited at a substrate temperature of 350 °C and an Ar pressure of 5 mTorr. Cr underlayers were deposited both at 25 °C and at 350 °C and exhibited differen...
متن کاملThe effects of Ag underlayer and Pt intermediate layers on the microstructure and magnetic properties of epitaxial FePt thin films
In this work, Ag underlayers, which have a slightly larger lattice parameter than FePt, were found not only to induce epitaxial growth of the FePt films but also to reduce the temperature at which the atomic ordering occurred. Without using the Ag underlayer, the FePt film deposited onto the hydrofluoric acid etched-Si substrate was FCC disordered. When Ag underlayers were used the FePt unit ce...
متن کاملGrowth and Characterization of Iron Nanowires Into Anodized Aluminum Oxide Templates Using Electrodeposition Technique
The Fe nanowires were prepared by Ac electrodeposition method. The two steps anodized aluminum oxides (alumina) were used as templates for electrodeposition of magnetic nanowires. Sulfuric acid was used to anodize aluminum. The pours diameter and growth rate of alumina were investigated. The FeSO4 electrolyte was used for growth of nanowires. The prepared magnetic nanowires were characterized b...
متن کاملarchitecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولCommensurate vortex pinning in Nb films patterned onto anodized aluminum oxide
Anodic aluminum oxide templates containing extended arrays of holes with 30-nm diameter and approximately 128-nm spacing were sputter-coated with Nb. We find pronounced matching effects in the transport and magnetization measurements beyond 4 kOe. In addition, we observe Little–Parks oscillations of the superconducting critical temperature. We compare the flux pinning in the patterned samples t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2011
ISSN: 1742-6596
DOI: 10.1088/1742-6596/266/1/012048