Magnetic Properties of Hard Magnetic Fe-Pt Alloys in Dental Casts
نویسندگان
چکیده
منابع مشابه
Some magnetic properties of platinum-rich Pt-Fe alloys
2014 Measurements of magnetic susceptibility and spontaneous magnetization on face centred cubic platinum-iron alloys having compositions around Pt3Fe and also on alloys with lower iron contents, are reported. In the Pt3Fe superlattice region the alloys appear to be antiferromagnetic when ordered and ferromagnetic when disordered. The more dilute alloys are ferromagnetic, even down to 2 at. % o...
متن کاملMAGNETIC STATES INSTABILITY OF Pt-Fe ALLOYS
Neutron-diffraction measurements have been used to 'determine the temperature and composition dependences of the ordered single crystals of Pt-Fe alloys containing 32, 30.5 and 28 at% of iron. A qualitative model for the complex antiferromagnetic ordering in the system based on the experimental data and band structure calculations has been proposed. The ordered Pt-Fe alloys with more than 36 at...
متن کاملMagnetic properties and structure of Fe/Pt thin films
The structural transfqmation from fcc to fct and relevant magnetic properties of initially multilayered Fe/Pt films were studied. When the asdeposited FePt films were annealed at the temperature of 300°C and up, the fct-phase was formed. Rather square hysteresis loops and large coercivities were measured from the annealed films. The films annealed at 300°C retain a layered structure.
متن کاملHard magnetic properties of melt-spun Mn-Al-C alloys
Structural and magnetic characterization of Mnx−yAl100−x−yC2y (x = {50, 55}; y = {0, 1}) melt-spun ribbons is reported. To obtain the metastable ferromagnetic τ-phase, rapidly solidified alloys were annealed either in a vacuum furnace at 823 K or directly in the vibrating sample magnetometer under applied magnetic field. Optimal magnetic properties were demonstrated by Mn54Al44C2 samples proved...
متن کاملGrindability of dental magnetic alloys.
In this study, the grindability of cast magnetic alloys (Fe-Pt-Nb magnetic alloy and magnetic stainless steel) was evaluated and compared with that of conventional dental casting alloys (Ag-Pd-Au alloy, Type 4 gold alloy, and cobalt-chromium alloy). Grindability was evaluated in terms of grinding rate (i.e., volume of metal removed per minute) and grinding ratio (i.e., volume ratio of metal rem...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1997
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.21.377