Magnetic Properties of Exchange-Coupled α-Fe/Nd-Fe-B Multilayer Films Fabricated by Sputtering
نویسندگان
چکیده
منابع مشابه
High coercivity SmFeAlC thin films fabricated by multilayer sputtering
Multilayer sputtering of SmFe/C(Al) plus appropriate thermal processing has been used to fabricate SmFeC thin films with A1 substitution for Fe. It was found that the SmFeAlC thin films exhibited exceptionally high Coercivities. A coercivity of 28 kOe was realized for the thin film with structure of Ta( l000~) / lSmFe(40~~/ G(Al)(5,&)]~50/Ta(200@ with subsequent annealing at 650°C.
متن کاملHigh coercivity SmFeSiC films fabricated by multilayer sputtering
SmFeSiC thin films have been obtained by sputtering SmFe/C(Si) multilayers with a Ta underlayer on Si substrates and subsequently annali The coercivity of the SmF films strongly depends on the sputtering and annea itions. The influence of the thickness of the Ta underlayer, the thickness ratio of SmFe to C(Si), the argon pressure and heat treatment Inplane Coercivities up to 7.2 kOe and squaren...
متن کاملCHARACTERIZATION OF CO-FE MAGNETIC FILMS FABRICATED BY GALVANO-STATIC ELECTRODEPOSITION
In this research, nanocrystalline Co-Fe coatings were electrodeposited on copper substrate. The influence of current density on different properties of the films at two pH levels was investigated. All the coatings showed nodular structure with rougher morphology at higher current densities. Due to anomalous deposition at higher current density, the amount of iron content increased and reached i...
متن کاملThe soft magnetic properties of stripes fabricated using laser ablation of multilayer thin films
We examine the low frequency BH loop and complex permeability spectra of multilayer permalloy films laser processed to define samples consisting of stripes parallel to the as-deposited hard axis. We begin by examining different laser energy densities for groove definition in films of different thickness. We observe that for well coupled multilayer films with thin, 15 nm, spacer layers the demag...
متن کاملLarge variation of magnetic properties of amorphous Fe–Zr thin films with Ar pressure during sputtering
A large change is observed in the magnetic properties of amorphous Fe-Zr thin films sputtered at different Ar pressures. The change depends on the composition of the alloys and at compositions near 60 at.% Fe, for example, the magnetisation measured at 10 kOe increases 30-fold with an increase in the Ar pressure from 2 to 10 mTorr. The magnetic properties are well explained by a combination of ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1997
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.21.361