Magnetic Properties of Co/Pt Multilayer Dots.
نویسندگان
چکیده
منابع مشابه
The Perpendicular Magnetic Anisotropy of CoPt/Au Multilayer Films
We have studied the magnetic properties of Au (2 nm)/Co50Pt50 (3 nm)/Au (2 nm) multilayer films prepared on amorphous Al2O3/Si and (0 0 1) MgO substrates. The as-deposited films on both substrates are magnetically soft with an FCC structure and exhibit a perpendicular anisotropy. After annealing at 500 °C, the sample on the Al2O3/Si substrate has become magnetically isotropic but the sample on ...
متن کاملMagnetic Properties of Nanostructured CoPt and FePt Thin Films
Polycrystalline MgO underlayer films lead to different preferred orientations of 10 CoPt and FePt films after the annealing process, depending on the thickness of 10 films. 10 films with a thickness greater than 20 nm revealed mostly 10 [100] fiber texture and consequently in-plane anisotropy as determined by magnetic hysteresis. Strong perpendicular anisotropy due to the 10 [001] fiber texture...
متن کاملMagnetic Properties of Exchange-Biased Multilayer With Perpendicular Magnetic Anisotropy
Perpendicular exchange-biased and multilayers have been fabricated, changing the thickness of the cobalt that is next to the IrMn layer. The crystal structure, interface roughness and magnetic properties were characterized by X-ray diffraction (XRD), X-ray reflectivity (XRR), atomic force microscopy (AFM) and extraordinary Hall Effect (EHE). The multilayers are flat, and the roughness is about ...
متن کاملThe effect of CoPt crystallinity and grain texturing on properties of exchange-coupled Fe/CoPt systems
exchange-coupled Fe/CoPt systems H. Oguchi, A. Zambano, M. Yu, J. Hattrick-Simpers, D. Banerjee, Y. Liu, Z. L. Wang, J. P. Liu, S. E. Lofland, D. Josell, and I. Takeuchi Department of Materials Science and Engineering, University of Maryland, College Park, Maryland 20742, USA Advanced Materials Research Institute, University of New Orleans, Louisiana 70148, USA School of Materials Science and E...
متن کاملStructure and magnetic properties of L10 CoPt„AgÕMgO,MgO... thin films
Disordered fcc ~face-centered-cubic! @100# fiber-textured CoPt thin films with thicknesses of 20–40 nm were deposited on a nonmagnetic sputtered MgO seed layer with and without a Ag intermediate layer. These were subsequently annealed at 600–750 °C for 5–10 min using rapid thermal annealing ~RTA!. The structural variants were determined to coexist in the in-plane and normal to the plane directi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 2001
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.25.859