Magnetic behavior of melt-spun gadolinium

Magnetic properties and synthesis conditions of Nd2Fe23B3 melt-spun alloy

The formation of amorphous and crystalline state of the Nd2Fe23B3 alloy from melt-spun ribbon is presented. The synthesis conditions are investigated combining DSC, X-ray diffraction and thermomagnetic analysis. The thermomagnetic analysis is found to be very useful to optimize the synthesis process. Comparison of these results enables to discuss the thermal stability of both the amorphous and ...

Hard magnetic properties of melt-spun Mn-Al-C alloys

Structural and magnetic characterization of Mnx−yAl100−x−yC2y (x = {50, 55}; y = {0, 1}) melt-spun ribbons is reported. To obtain the metastable ferromagnetic τ-phase, rapidly solidified alloys were annealed either in a vacuum furnace at 823 K or directly in the vibrating sample magnetometer under applied magnetic field. Optimal magnetic properties were demonstrated by Mn54Al44C2 samples proved...

The Structure and Magnetic Properties of Co77Zr18W5 Melt-Spun Ribbons

Based on X-ray diffraction, microscopic and magnetic analysis, the structure and magnetic properties of Co77Zr18W5 melt-spun ribbons were studied in this paper. A new element to stabilize the metastable Co5Zr phase was found and the coercivity observed in Co-Zr alloys can be obviously enhanced by proper tungsten substitution. The Curie temperature of Co77Zr18W5 ribbons is 475 ̊C which suggests t...

Effects of nanoscale disorder on the paramagnetic to ferromagnetic transition in melt-spun gadolinium and gadolinium iron alloys

Mechanical response of melt-spun amorphous filaments

High-speed melt spinning of a cyclo-olefin polymer (COP) and a copolyamide (CoPA) have been performed. Differential scanning calorimetry curves of the resulting monofilaments show that they remain in an amorphous state even after hot drawing. Wide angle x-ray diffraction patterns of undrawn and drawn COP filaments show that although the material remains in an amorphous state, a degree of orient...