Magnetic and electrical properties of yttrium substituted manganese ferrite nanoparticles prepared via micro-emulsion route
نویسندگان
چکیده
منابع مشابه
Physical and magnetic properties of highly aluminum doped strontium ferrite nanoparticles prepared by auto-combustion route
Highly Al3þ ion doped nanocrystalline SrFe12 xAlxO19 (0rxr12), were prepared by the auto-combustion method and heat treated in air at 1100 1C for 12 h. The phase identification of the powders performed using x-ray diffraction show presence of high-purity hexaferrite phase and absence of any secondary phases. With Al3þ doping, the lattice parameters decrease due to smaller Al3þ ion replacing Fe3...
متن کاملPreparation and investigation of magnetic properties of Manganese Cadmium ferrite nanoparticles by Sol-gel method
In the present investigation, manganese ferrite nanoparticles substituted by cadmium with Mn1-xCdxFe2O4 composition and substituted amount x=(0, 0.1, 0.3, 0.5) were prepared by Sol-gel method. Pattern analysis of X-ray diffraction (XRD) confirmed ferrite single phase structure in all samples. The average crystal size was estimated from 17 to 22 nm. The chemical bonds and ferrite formation phase...
متن کاملSynthesis and magnetic investigation of cobalt ferrite nanoparticles prepared via a simple chemical precipitation method
In this research cobalt ferrite (CoFe2O4) nano-crystalline powders were prepared by simple chemical precipitation method using cobalt sulfate. The CoFe2O4 nanoparticles were characterized by X-ray diffraction, scanning electron microscopy and Fourier transform infra-red spectroscopy. The crystallite size of CoFe2O4 nanoparticles was calculated by Debye–Scherrer formula. The effect of precursor...
متن کاملMorphology and magnetic characterisation of aluminium substituted yttrium-iron garnet nanoparticles prepared using sol gel technique.
Aluminum substituted yttrium iron garnet nano particles with compositional variation of Y(3.0-x) A1(x)Fe5O12, where x = 0.0, 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0 were prepared using sol gel technique. The X-ray diffraction results showed that the best garnet phase appeared when the sintering temperature was 800 degrees C. Nano-crystalline particles with high purity and sizes ranging from 20 to 100 n...
متن کاملCation Distribution in Lithium Ferrite (LiFe5O8) Prepared via Aerosol Route
Nano size lithium ferrite was prepared through aerosol route and characterized using TEM, XRD, magnetic measurements and Mössbauer spectroscopy. The particle size of as obtained samples were found to be ~10 nm through TEM, that increases upto ~80 nm on annealing at 1200 C. The unit cell parameter ‘a’ calculated using XRD, confirms the formation of α-LiFe5O8. Room temperature Mössbauer spectra o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Results in Physics
سال: 2020
ISSN: 2211-3797
DOI: 10.1016/j.rinp.2020.102973