Machinability of Experimental Ti-Cu Alloys
This study is an investigation of the machinability of experimental Ti-Cu alloys (2, 5, and 10mass% Cu) as new dental titanium alloy candidates for CAD/CAM use. The alloys were slotted with a vertical milling machine and carbide square end mills under two cutting conditions. Their machinability was evaluated through cutting force using a three-component force transducer fixed on the table of th...
متن کاملMachinability of experimental Ti-Ag alloys.
This study investigated the machinability of experimental Ti-Ag alloys (5, 10, 20, and 30 mass% Ag) as a new dental titanium alloy candidate for CAD/CAM use. The alloys were slotted with a vertical milling machine and carbide square end mills under two cutting conditions. Machinability was evaluated through cutting force using a three-component force transducer fixed on the table of the milling...
متن کاملThermodynamic and experimental study of Ti-Ag-Cu alloys
Phase equilibria in the ternary Ti-Ag-Cu system have been studied thermodynamically and experimentally at various temperatures. The thermodynamic analysis was performed by combining the most recent data on the binary Ag-Cu, Ti-Ag and Ti-Cu systems and experimental information obtained by the diffusion couple technique. The eutectic and three noneutectic binary Ag-Cu alloys were melted and annea...
متن کاملCorrosion Characteristics of a - Ti and Ti 2 Cu Composing Ti - Cu Alloys
A series ef binary Ti-Cu alloys containing 5-20 mass% Cu was prepared, and the corresien behavior of a-Ti and Ti2Cu composing the Ti-Cu alloys were examined based on the anodic polarization curves and released iens in O.9% NaCl and 1% lactic acid solutions. In both selutions, the Ti-Cu alloys showed the same anodic polarization curves as titanium in the conditien below 1.4 V. Hewever, precipita...
متن کاملMechanical properties and microstructures of dental cast Ti-Ag and Ti-Cu alloys.
In this study, experimental Ti-Ag alloys (5, 10, and 20 mass% Ag) and Ti-Cu alloys (2, 5, and 10 mass% Cu) were made in an argon-arc melting furnace. The alloys were cast into magnesia molds using an argon gas-pressure dental casting machine, and the mechanical properties and microstructures of the castings were investigated. As the concentration of silver or copper in the alloys increased, the...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2008
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.mra2007285