Lubricated wear resistance of Al-Cu-Mn-Mg-Si and Al-Si-Cu-Mn-Mg alloys to ADC12 die cast alloy.

Fluidized Bed Heat Treatment of Cast Al-Si-Cu-Mg Alloys

The effects of fluidized bed heat treatment on the microstructural and mechanical properties of Al-Si-Cu-Mg cast alloys, namely,3 54 and 319, were studied. The heating rate in fluidized beds (FBs) is greater vis-a`-vis conventional electrical resistancef urnaces (CFs). The high heating ratei nF Bs increases the kinetics of metallurgical phenomena such as Si fragmentation and spherodization duri...

Precipitation Hardening of Al–Si–Mg Alloys

SOLUTION STRENGTHENING AND AGE HARDENING CAPABILITY OF Al-Mg-Mn ALLOYS WITH SMALL ADDITIONS OF Cu

Nine Al-(1-3)Mg-(0-0.4)Cu-0.15Si-0.25Mn (in wt%) alloys with potential applications in both packaging and automotive industries have been investigated. Tensile testing showed that solution strengthening is in good approximation linearly proportional to the Mg content. Mechanical testing and microstructural examinations of aged samples indicate that Mg2Si phase precipitates contribute to age har...

Microstructure and Precipitation in Al - Li - Cu - Mg - ( Mn , Zr ) alloys

Hot rolled Al-6Li-1Cu-1Mg-0.2Mn (at.%) (Al-1.6Li-2.2Cu-0.9Mg-0.4Mn, wt.%) and Al-6Li-1Cu-1Mg-0.03Zr (at.%) (Al-1.6Li-2.3Cu-1Mg-0.1Zr, wt.%) alloys developed for age forming were studied by tensile testing, electron backscatter diffraction (EBSD), three-dimensional atom probe (3DAP), transmission electron microscopy (TEM) and differential scanning calorimetry (DSC). For both alloys, DSC analysis...

Dsc Study of Precipitation in an Al-mg-mn Alloy Microalloyed with Cu

Power compensation DSC has been employed to detect and analyse precipitation reactions in an Al1.3Mg-0.4Mn and an Al-1.3Mg-0.4Mn-0.07Cu alloy in which very small amounts of precipitate, less than 0.3 at%, are expected to form. Due to the very small heat effects, baseline instability and drift significantly interfere with the measurements. After repeated experiments and careful baseline correcti...