Low-temperature synthesis of calcium hexaboride nanoparticles via magnesiothermic reduction in molten salt
نویسندگان
چکیده
منابع مشابه
LOW TEMPERATURE MOLTEN SALT SYNTHESIS OF NANO CRYSTALLINE MgAl2O4 POWDER
Abstract: composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nanopowder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) techniques. It was demonstrated tha...
متن کاملElectrochemical Synthesis of Magnesium Hexaboride by Molten Salt Technique
The present work reports electrochemical synthesis of MgB6 from molten salts using the precursor consists of LiF-B2O3-MgCl2. An attempt has been made to synthesize metastable phase MgB6 crystal by electrolysis method. DTA/TGA studies were made to determine the eutectic point of the melt and it was found to be around 900°C. The electrolysis was performed at 900°C under argon atmosphere, at curre...
متن کاملLow temperature synthesis of CaZrO3 nanoceramics from CaCl2–NaCl molten eutectic salt
CaZrO3 nanoceramics were successfully synthesized at 700 C using the molten salt method, and the effects of processing parameters, such as temperature, holding time, and amount of salt on the crystallization of CaZrO3 were investigated. CaCl2, Na2CO3, and nano-ZrO2 were used as starting materials. On heating, CaCl2–NaCl molten eutectic salt provided a liquid medium for the reaction of CaCO3 an...
متن کاملMolten Salt Synthesis of Calcium Hydroxyapatite Whiskers
Calcium hydroxyapatite (HA) whiskers and crystals were produced by the route of molten salt synthesis. The effects on whisker morphology of chosen flux, flux-to-HA ratio, synthesis temperature, and reaction time were investigated. The thermal stabilities of the produced whiskers were tested at 1300°C in an air atmosphere. A tentative X-ray diffraction pattern was proposed for the HA whiskers. M...
متن کاملlow temperature synthesis of cazro3 nanoceramics from cacl2–nacl molten eutectic salt
cazro3 nanoceramics were successfully synthesized at 700 c using the molten salt method, and the effects of processing parameters, such as temperature, holding time, and amount of salt on the crystallization of cazro3 were investigated. cacl2, na2co3, and nano-zro2 were used as starting materials. on heating, cacl2–nacl molten eutectic salt provided a liquid medium for the reaction of caco3 an...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2017
ISSN: 1348-6535,1882-0743
DOI: 10.2109/jcersj2.17102