Low Friction CrNMPP/TiNDCMS Multilayer Coatings
نویسندگان
چکیده
منابع مشابه
Low Friction CrNMPP/TiNDCMS Multilayer Coatings
Transition metal nitrides like CrN and TiN are widely used in automotive applications due to their high hardness and wear resistance. Recently, we showed that a multilayer architecture of CrN and TiN, deposited using the hybrid-high power impulse magnetron sputtering (HIPIMS) and direct current magnetron sputtering (DCMS)-HIPIMS/DCMS deposition technique, results in coatings which indicate not ...
متن کاملSelf-lubricating, low-friction, wear-resistant Al-based quasicrystalline coatings
After gas atomization, a quasicrystalline powder based on aluminium was used to prepare a thick coating by high-velocity oxygen-fuel flame torch spraying. This layer was deposited on top of a bond-coat layer on a steel plate. A post-spraying annealing treatment turned the two layers to their stable state, a γ-brass crystal and an icosahedral quasicrystal, respectively. The projection parameters...
متن کاملEllipsometry of light scattering from multilayer coatings.
A scatterometer is extended and allows us to perform ellipsometric measurements on scattered light in each direction of space. Experimental data are given for single thin-film layers and optical coatings and reveal unexpected results. The phenomena are investigated by means of the electromagnetic theories of surface and bulk scattering that emphasize the role of partial correlation and localize...
متن کاملDelamination of multilayer thermal barrier coatings
Multilayer thermal barrier coatings (TBCs) on superalloy substrates are comprised of an intermetallic bond coat, a thermally grown oxide (TGO) layer, and a porous zirconia top coat that provides thermal protection. The TGO attains a thickness of 1±10 lm prior to failure, while the bond coat and zirconia layer are each about 50±100 lm thick. The preferred method for manufacturing TBCs comprises ...
متن کاملLow Friction, High Endurance Ion-Beam Deposited Pb-Mo-S Coatings
Thin solid lubricating coatings of Pb-Mo-S were deposited on steel substrates via ion-beam deposition. Coating endurance and friction coefficients under dry air sliding conditions were monitored with ball-on-disk tests; additional tribological testing was performed using a ball-on-flat reciprocating test rig to investigate intermediate sliding distances (100-32000 cycles). Rutherford backscatte...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tribology Letters
سال: 2012
ISSN: 1023-8883,1573-2711
DOI: 10.1007/s11249-012-9922-y