Low-firing, temperature stable and improved microwave dielectric properties of ZnO TiO2Nb2O5 composite ceramics

LOW-TEMPERATURE SINTERING AND MICROWAVE DIELECTRIC PROPERTIES OF (Zn0.65Mg0.35)TiO3-CaTiO3 CERAMICS WITH H3BO3 ADDITION

Low-melting H3BO3, acting as sintering aid, was used to reduce the sintering temperature of 5 wt.% CaTiO3-doped (Zn0.65Mg0.35)TiO3 ceramics. The sintering behaviors, microstructures and microwave dielectric properties with different amounts of H3BO3 addition were investigated. The results showed that H3BO3 additive was very effective for lowering the sintering temperature and improving the bulk...

Crystal Structure, Infrared Spectra and Microwave Dielectric Properties of Temperature Stable Zircon-Type (Y,Bi)VO4 Solid Solution Ceramics

High frequency dielectric properties of A5B4O15 microwave ceramics

High-frequency dielectric properties of A5B4O15 ~A5Ba, Sr, Mg, Zn, Ca; B5Nb, Ta! dielectric ceramics are studied by means of the microwave cavity technique, a combination of far-infrared reflection and transmission spectroscopy and time-resolved terahertz transmission spectroscopy. Microwave permittivity e8 and Q3 f factor vary, depending on the chemical composition, between 11 and 51, and 2.4 ...

Effect of Calcination Kinetics and Microwave Sintering Parameters on Dielectric and Peizo-Electric Properties of(K0.5Na0.5) NBO3 Ceramics

An efficient solid-state approach was established to synthesize (K0.5Na0.5) NbO3 ceramics using calcination kinetics and microwave assisted sintering. Milling of carbonate and oxide raw materials were carried out for 15h to obtain homogeneous nano particles. The crystallite size of 5.30 nm was obtained for the KNN system after calcination through optimized parameters and observed to be stoichio...

Nb-Doped 0.8BaTiO3-0.2Bi(Mg0.5Ti0.5)O3 Ceramics with Stable Dielectric Properties at High Temperature

Nb-doped 0.8BaTiO3-0.2Bi(Mg0.5Ti0.5)O3 ceramics were prepared by conventional solid-state method. The dielectric properties and the structural properties were investigated. When Nb2O5 is doped into 0.8BT-0.2BMT system, a small amount of Ba4Ti12O27 secondary phase is formed. The lattice parameters gradually increase with the Nb2O5 doping. It is found that the temperature-capacitance characterist...