Low Cycle Fatigue of Steel in Strain Controled Cyclic Bending
نویسندگان
چکیده
منابع مشابه
Energy-Based Prediction of Low-Cycle Fatigue Life of CK45 Steel and SS316 Stainless Steel
In this paper, low cycle fatigue life of CK45 steel and SS316 stainless steel under strain-controlled loading are experimentally investigated. In addition, the impact of mean strain and strain amplitude on the fatigue life and cyclic behavior of the materials are studied. Furthermore, it is attempted to predict fatigue life using energy and SWT damage parameters. The experimental results demons...
متن کاملBending Fatigue Failures in Valve Steel
In the present paper the effect of defects (viz. pits, gouges and oxide inclusions) will be reported. Although certain defects were uniformly distributed over the specimen surface, the majority of all fractures started in the edge region. An explanation to this behaviour is presented in terms of stress enhancement in the edge regions due to edge deflections.
متن کاملIdentification of Low Cycle Fatigue Parameters of High Strength Low-alloy (hsla) Steel at Room Temperature
S. Bulatović, Yugoslav River Shipping, Serbia, Lj. Milović, University of Belgrade, Faculty of Technology and Metallurgy, Serbia, A. Sedmak, University of Belgrade, Faculty of Mechanical Engineering, Serbia, I. Samardžić, University of Osijek, Mechanical Engineering Faculty, Slavonski Brod, Croatia Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of ...
متن کاملAssessment of different methods for fatigue life prediction of steel in rotating bending and axial loading
Generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. The present paper investigates the effect of a notch on the fatigue life of the HSLA100 (high strength low alloy) steel which is widely applicable in the marine industry. Tensile test was conducted on specimens and mechanical properties were obtain...
متن کاملStatic Strain Aging Behavior of Low Carbon Steel Drawn Wire
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Mechanica et Automatica
سال: 2016
ISSN: 2300-5319
DOI: 10.1515/ama-2016-0011