Low-Cycle Fatigue Crack Growth in Ti-6242 at Elevated Temperature
نویسندگان
چکیده
منابع مشابه
Mixed-mode, high-cycle fatigue-crack growth thresholds in Ti– 6Al–4V: Role of small cracks
There have been few studies to date describing fatigue-crack propagation thresholds under mixed-mode loading conditions in the presence of cracks, that are small as compared to the characteristic microstructural dimensions. To address this need, the variation in mixed-mode, high-cycle fatigue-crack growth thresholds with crack size is reported for a Ti-6Al-4V turbine blade alloy with a fine-gra...
متن کاملMixed-mode, high-cycle fatigue-crack growth thresholds in Ti±6Al±4V II. Quanti®cation of crack-tip shielding
The role of crack-tip shielding in in ̄uencing mixed-mode (mode I II) fatigue-crack growth thresholds for large, through-thickness cracks in a Ti±6Al±4V turbine blade alloy is examined under high-cycle fatigue loading conditions, i.e., at a loading frequency of 1000 Hz in ambient temperature air for load ratios (Kmin=Kmax) of R 0:1±0.8. Techniques are developed to quantify crack-tip shielding...
متن کاملMixed-Mode, High-Cycle Fatigue-Crack Growth Thresholds in Ti-6Al-4V: A Comparison of Large and Small Crack Behavior
There are few experimental results to date describing the crack-propagation threshold behavior of short fatigue cracks under multiaxial loading conditions. To address this need, in the present study, the variation in mixed-mode, high-cycle fatigue-crack growth thresholds with crack size and shape are reported for a Ti-6Al-4V turbine blade alloy, heat treated to two widely different microstructu...
متن کاملShort and Large Crack , Mixed - Mode Fatigue - Crack Growth Thresholds in Ti - 6 Al - 4 V
There are few experimental results to date describing the crack-propagation threshold behavior of short fatigue cracks under multiaxial loading conditions. To address this need, in the present study, the variation in mixed-mode, high-cycle fatigue-crack growth thresholds with crack size and shape are reported for a Ti-6Al-4V turbine blade alloy, heat treated to two widely different microstructu...
متن کاملHigh-Temperature Cyclic Fatigue-Crack Growth in Monolithic Ti3SiC2 Ceramics
identical slip planes) and walls or kink boundaries. Thus, in addition to regular slip, mechanisms for ambient temperature The cyclic fatigue behavior of reactive hot-pressed Ti3SiCz plastic deformation in Ti3SiCz are thought to involve the ceramics are examined at temperatures from ambient to 1200°C readjustment of local stress and strain fields from kink band with the objective of characteriz...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advanced Materials Research
سال: 2014
ISSN: 1662-8985
DOI: 10.4028/www.scientific.net/amr.891-892.422