Low-Cycle Corrosion-Fatigue of Pre-Strained Steel
نویسندگان
چکیده
منابع مشابه
Energy-Based Prediction of Low-Cycle Fatigue Life of CK45 Steel and SS316 Stainless Steel
In this paper, low cycle fatigue life of CK45 steel and SS316 stainless steel under strain-controlled loading are experimentally investigated. In addition, the impact of mean strain and strain amplitude on the fatigue life and cyclic behavior of the materials are studied. Furthermore, it is attempted to predict fatigue life using energy and SWT damage parameters. The experimental results demons...
متن کاملHigh-Cycle Microscopic Corrosion Fatigue Behavior and Life Prediction of 25CrMo Steel Used in Railway Axle
The effects of environmental media on the corrosion fatigue fracture behavior of 25CrMo steel were investigated. The media include air, and a 3.5 wt.% and a 5.0 wt.% NaCl solutions. Experimental results indicate that the media induces the initiation of corrosion fatigue cracks at multiple sites. The multi-cracking sites cause the changes in the crack growth directions, the crack growth rate dur...
متن کاملFatigue of Reinforcing Steel Bars Subjected to Natural Corrosion
Under badly environmental conditions as well as complex loads, corrosion of embedded reinforcing steel bars in concrete is common for reinforced concrete (RC) structures. Fatigue of corrosion reinforcing steel bars is a key problem for old RC bridges. To assess the residual fatigue life of aged existing RC bridges, the most new study information on fatigue of natural corrosion reinforcement is ...
متن کاملIdentification of Low Cycle Fatigue Parameters of High Strength Low-alloy (hsla) Steel at Room Temperature
S. Bulatović, Yugoslav River Shipping, Serbia, Lj. Milović, University of Belgrade, Faculty of Technology and Metallurgy, Serbia, A. Sedmak, University of Belgrade, Faculty of Mechanical Engineering, Serbia, I. Samardžić, University of Osijek, Mechanical Engineering Faculty, Slavonski Brod, Croatia Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of ...
متن کاملThe Effect of Pre-strain on Fatigue for a High Strength Low Alloy (hsla)steel
D. Aguirre-Guerrero, A. Juárez-Hernández, M.A.L. Hernández-Rodríguez, University Autonumous of Nuevo León, Faculty of Mechanical and Electrical Engineering, Nuevo León, México. R. Morales, I. Ruiz, PEMSA Co. Celaya, Guanajuato, México. The eff ect of initial plastic strain c ycle fatigue lives of HSLA specimens is in vestigated. Specimens were monotonically, quasi-statically loaded under strain...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: CORROSION ENGINEERING DIGEST
سال: 1965
ISSN: 0010-9355,1884-1155
DOI: 10.3323/jcorr1954.14.5_197