Liquid-phase sintering of lead borosilicate glass-alumina composite
نویسندگان
چکیده
منابع مشابه
Sintering behaviour of composite materials borosilicate glass-ZrO2 fibre composite materials
The characteristics and properties of mixtures of a borosilicate glass and ZrO2 fibres obtained from compacts isothermally sintered are presented. Three different particle sizes of glass powder and different sintering temperatures and times have been used to reveal the influence of the specific surface area and the glass matrix viscosity on sintering. The fundamental developed aspects are the s...
متن کاملLiquid–liquid phase separation in alkali-borosilicate glass. An impedance spectroscopy study
We followed the first stages of liquid–liquid phase separation in an alkali-borosilicate glass by complex impedance spectroscopy at constant temperatures below and above the glass transition temperature, Tg. We found a new feature of the electrical conductivity behavior: at temperatures below Tg, the electrical conductivity, r, diminished with time, while above Tg, the electrical conductivity i...
متن کاملMagnetic Glass Ceramics by Sintering of Borosilicate Glass and Inorganic Waste
Ceramics and glass ceramics based on industrial waste have been widely recognized as competitive products for building applications; however, there is a great potential for such materials with novel functionalities. In this paper, we discuss the development of magnetic sintered glass ceramics based on two iron-rich slags, coming from non-ferrous metallurgy and recycled borosilicate glass. The s...
متن کاملLow-Temperature Sintering of Alumina with Liquid-Forming Additives
Simultaneous application of colloidal processing and liquidforming additives to alumina resulted in a sintered density of >99% in 1 h at a temperature as low as 1070°C for a commercial high-purity alumina powder at a total dopant level of 2 mol%. The additives were 0.9% CuO + 0.9% TiOz + 0.1% B 2 0 3 + 0.1% MgO. At higher temperatures or after prolonged sintering, the doped alumina ceramic deve...
متن کاملQuantitative AFM analysis of phase separated borosilicate glass surfaces
Phase separated borosilicate glass samples were prepared by applying various heat treatments. Using selective chemical etching we performed AFM measurement on the phase separated glass surfaces. A quantitative roughness analysis allowed us to measure precisely the dependence of the characteristic size of the phase domains on heating time and temperature. The experimental measurements are very w...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Science Letters
سال: 1990
ISSN: 0261-8028,1573-4811
DOI: 10.1007/bf00721796