Liquid Phase Boundaries at 1873K in the Ternary CaO-Al2O3-MOX(MOX: MgO, ZrO2) and CaO-SiO2-MOx(MOx: TiO2, MgO, Al2O3) Systems.

Ternary System Al2O3–MgO–CaO: I, Primary Phase Field of Crystallization of Spinel in the Subsystem MgAl2O4–CaAl4O7–CaO–MgO

Using a novel experimental procedure in the field of ceramics/materials science that is based on the precise microanalysis (scanning electron microscopy, coupled with wavelength-dispersive spectroscopy) of the phases that are present in equilibrated specimens, the solid-state compatibility relations in the subsystem MgAl2O4–CaAl4O7–CaO– MgO and the melting relationships in the subsystems MgAl2O...

Experimental Establishment of the CaAl2O4–MgO and CaAl4O7–MgO Isoplethal Sections within the Al2O3–MgO–CaO Ternary System

The isoplethal sections CaAl2O4–MgO and CaAl4O7–MgO of the Al2O3–MgO–CaO ternary system have been experimentally established at 1 bar total pressure and air of normal humidity. The sections obtained provide new data and information that are in disagreement with thermodynamic evaluations and optimizations of the Al2O3–MgO–CaO ternary system published to date. These differences arise mainly from ...

A thermodynamic assessment of the BaO-MgO, BaO-CaO, BaO-Al2O3 and BaO-SiO2 systems

Aalto University, P.O. Box 11000, FI-00076 Aalto www.aalto.fi Author Rui Zhang, Pekka Taskinen Name of the publication Publisher School of Chemical Technology Unit Department of Materials Science and Engineering Series Aalto University publication series SCIENCE + TECHNOLOGY 4/2014 Field of research Metallurgy

Kinetics of spinel formation and growth during dissolution of MgO in CaO-Al2O3-SiO2 slag

Thermodynamic simulation on mineralogical composition of CaO–SiO2–Al2O3–MgO quaternary slag system

It is necessary to elucidate the crystallization thermodynamic of mineralogical phases during the cooling process of the molten BFS with different chemical composition, because the high-melting point mineral phase maybe crystallized during the fiber forming and thereafter cooling process. Thermodynamic calculation software FactSage6.4 and the hot remelting experiments were performed to explore ...