Life Assessment in Boundary between Phenomena of Fatigue and Corrosion Fatigue

Fatigue and corrosion fatigue properties of Ti-6Al-4V implant grade titanium alloy in Ringer solution

Nowadays modification of metallic biomaterials which are used as implants for bone and hard tissues replacement is considered as an important subject. In the current study, corrosion fatigue properties of Ti-6Al-4V alloy investigated via Rotating-Bending standard test method and then, the results compared with the fatigue properties of the specimens tested in the same conditions. Scanning elect...

Fracture Mechanics and Corrosion Fatigue

The development and current state-of-the-art in fracture mechanics in relation to studies of environment-enhanced fatigue-crack growth (corrosion fatigue) and fatigue-crack growth per se are reviewed. Patterns of response of materials to different loading and environmental conditions are considered in terms of the probable mechanisms for environmental embrittlement. The usefulness of the fractu...

High-Strength Bolt Corrosion Fatigue Life Model and Application

The corrosion fatigue performance of high-strength bolt was studied. Based on the fracture mechanics theory and the Gerberich-Chen formula, the high-strength bolt corrosion fracture crack model and the fatigue life model were established. The high-strength bolt crack depth and the fatigue life under corrosion environment were quantitatively analyzed. The factors affecting high-strength bolt cor...

Thermo-Mechanical Fatigue Life Assessment of a Diesel Engine Piston

Assessment of different methods for fatigue life prediction of steel in rotating bending and axial loading

Generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. The present paper investigates the effect of a notch on the fatigue life of the HSLA100 (­high strength low alloy) steel which is widely applicable in the marine industry. Tensile test was conducted on specimens and mechanical properties were obtain...