Laser Welding of Magnesium Alloy
نویسندگان
چکیده
منابع مشابه
Laser Welding of Magnesium Alloys
Aiming at establishing a reliable welding technique for magnesium alloys, the laser weldability of different types of magnesium alloys has been investigated using a high-brightness disc laser. It was found that high quality joints could be fabricated in the case of wrought type alloys when a certain defocusing level was optimized for the employed high-brightness laser beam of the newly develope...
متن کاملLaser Welding of Aluminium Alloy 5083
There are two laser welding mechanisms, keyhole mode and conduction mode. Keyhole welding is widely used because it produces welds with high aspect ratios and narrow heat affected zones. However keyhole welding can be unstable, as the keyhole oscillates and closes intermittently. This intermittent closure causes porosity due to gas entrapment. Conduction welding, on the other hand, is more stab...
متن کاملLaser Welding of Thin Sheet Magnesium Alloys
Magnesium and its alloys are active materials, and the oxide can easily form when they react with air and moisture (Czerwinski 2002). In addition, magnesium and its alloys are flammable and require strict safeguards during the manufacturing process. These disadvantages make the processing of magnesium alloys into finished products more challenging. These drawbacks cause defects such as cracks, ...
متن کاملAnalysis and Comparison of Friction Stir Welding and Laser Assisted Friction Stir Welding of Aluminum Alloy
Friction Stir Welding (FSW) is a solid-state joining process; i.e., no melting occurs. The welding process is promoted by the rotation and translation of an axis-symmetric non-consumable tool along the weld centerline. Thus, the FSW process is performed at much lower temperatures than conventional fusion welding, nevertheless it has some disadvantages. Laser Assisted Friction Stir Welding (LAFS...
متن کاملOptimization of TIG repair welding process parameters to obtain maximum tensile strength in AZ91C magnesium alloy
In this study, in order to modify the weld structure obtained from repair welding of AZ91C magnesium alloy and improvement of tensile strength, input parameters such as current intensity and preheating temperature were optimized for this alloy. T6 heat treatment was separately done befor and after the welding to homogenize the microstructure and improvement of the mentioned properties. Using va...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: DEStech Transactions on Social Science, Education and Human Science
سال: 2017
ISSN: 2475-0042
DOI: 10.12783/dtssehs/aetms2017/15891