Laser treatments of Nimonic 263 nickel-based superalloy
نویسندگان
چکیده
منابع مشابه
Nimonic 263 Microstructure and Surface Characterization after Laser Shock Peening
P. Drobnjak, High Technical School “Tehnikum-Tau runum”, Belgrade, Serbia, A. Kovačević, Institute of Physics, University of Belgrade, Serbia, A.Milosav lje vić, Faculty of Mechanical Engineering, University of Belgrade, Serbia, Ž. Radovanović, Faculty of Tech no lo gy and Metallurgy, University of Belgrade, Ser bia, I. Samardžić, Faculty of Mechanical Engine ering, Slavonski Brod, University o...
متن کاملLaser Cladding of Ultra-Thin Nickel-Based Superalloy Sheets
Laser cladding is a well-established process to apply coatings on metals. However, on substrates considerably thinner than 1 mm it is only rarely described in the literature. In this work 200 µm thin sheets of nickel-based superalloy 718 are coated with a powder of a cobalt-based alloy, Co-28Cr-9W-1.5Si, by laser cladding. The process window is very narrow, therefore, a precisely controlled Yb ...
متن کاملAnalysis of Cracks in the Pulsed Nd:YAG Laser Welded Joint of Nickel-Based Superalloy
The weldability of GTD-111 nickel-based superalloy by pulsed Nd:YAG laser welding with an average power of 250 W was studied, and the microstructural evolution and cracking characteristics were also investigated. The solidification cracking of the fusion zone (FZ) and the intergranular liquation cracking in the heat affected zone (HAZ) were observed in the joint. Solidification cracking was cau...
متن کاملJoining of nickel-base superalloy single crystals
Introduction ................................................................................................................................1 Overview of Weldability of Nickel-Base Superalloys..................................................................1 Crystallography............................................................................................................................
متن کاملPrediction of the Hot Compressive Deformation Behavior for Superalloy Nimonic 80A by BP-ANN Model
Abstract: In order to predict hot deformation behavior of superalloy nimonic 80A, a back-propagational artificial neural network (BP-ANN) and strain-dependent Arrhenius-type model were established based on the experimental data from isothermal compression tests on a Gleeble-3500 thermo-mechanical simulator at temperatures ranging of 1050–1250 ̋C, strain rates ranging of 0.01–10.0 s ́1. A comparis...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Zastita materijala
سال: 2019
ISSN: 0351-9465,2466-2585
DOI: 10.5937/zasmat1901026p