Laser processing and microstructure of Al-Cu-Fe quasicrystalline coatings on Al-base materials
نویسندگان
چکیده
منابع مشابه
Laser processing and microstructure of Al-Cu-Fe quasicrystalline coatings on Al-base materials
There is a large interest in using high power lasers for surface alloying or cladding on aluminium alloys, in order to enhance hardness and to improve wear resistance. A partly quasicrystalline surface layer (QC) (Al-Cu-Fe coating) has been obtained by laser cladding on Al-base materials. In addition to crystalline phases (Al5Fe2 and AlisFe4t -with dissolved copper), a quasicrystalline Al-Cu-Fe...
متن کاملStable Quasicrystalline Phase in Al-Cu-Fe-Cr Coating Materials
Transmission electron microscopy (TEM) studies have been carried out on magnetron-sputtered coatings in the Al-rich region of the Al-Cu-Fe-Cr quasicrystalline phase field, focusing on the composition that exhibited the best tribological performance among a group of sputtered coatings. The size of the particles in the as-deposited coating is around 10 nm. The TEM experiments on annealed coatings...
متن کاملMicrostructural evolution in Al–Cu–Fe quasicrystalline thin films
Transmission electron microscopy (TEM) was performed to study the microstructural evolution in Al–Cu–Fe quasicrystalline thin films. Thin films were grown by magnetron sputtering on sodium chloride crystals, which were subsequently dissolved in water to acquire free-standing films. Studies were conducted on the as-deposited sample, and samples that were annealed at 400 8C in Argon and 500 8C in...
متن کاملProcessing Of Al-Cu-Fe Single Grains
The phase equilibria of the Al-Cu-Fe quasicrystalline phase (y phase) is complex and conventional crystal growth techniques like the Bridgman and Czochralski methods are not applicable in preparation of large crystals. Large single grains of the y phase been have prepared by either slow cooling or isothermal anneals. In the later technique, arc melted ingots were subjected to either single or m...
متن کاملOxidative and tribological properties of amorphous and quasicrystalline approximant Al-Cu-Fe thin films.
The origins of the tribological properties and corrosion resistance of amorphous and quasicrystalline approximant alloys have been studied by comparing their properties in thin Al-Cu-Fe alloy films with compositions lying near the quasicrystalline region of the ternary compositional phase diagram. Six sputtered thin films of an Al-Cu-Fe alloy were studied using X-ray diffraction, X-ray photoemi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Le Journal de Physique IV
سال: 1994
ISSN: 1155-4339
DOI: 10.1051/jp4:1994434