Laboratory corrosion tests of welded low-carbon stainless steel
نویسندگان
چکیده
منابع مشابه
Liquid Metal Corrosion of 316L Stainless Steel, 410 Stainless Steel, and 1015 Carbon Steel in a Molten Zinc Bath
Corrosion tests of 1015 low-carbon steel and two stainless steels (410 and 316L) were conducted in a pure zinc bath (99.98 wt pct Zn) in order to better understand the reaction mechanisms that occur during the degradation of submerged hardware at industrial general (batch) galvanizing operations. Through this testing, it was found that, in general, 316L stainless steel showed the best dissoluti...
متن کاملCorrosion Behavior of Stainless Steel Clad Rebar
Stainless steel clad rebar (SCR) was investigated because it may become a cost-effective means of controlling corrosion in concrete under very aggressive environments. Sound SCR (316L cladding) resisted corrosion in saturated Ca(OH)2 solution (SCS) with up to 5 wt% chloride. Cladding breaks on SCR induced significant corrosion of exposed underlying CS in SCS with only 1 wt% chloride. A computer...
متن کاملCorrosion at Sulphide Inclusions in Stainless Steel
Auger analysis was performed using a high resolution scanning auger electron microscope and auger electron spectroscopy. Elemental auger contour maps for corroded sulphide inclusions in stainless steel were presented. It was found that the copper enriched-manganese sulphide inclusions were uniformly corroded, which might be due to CU2S deposition on the surface of corroding inclusions. In contr...
متن کاملProbabilistic Pitting Corrosion Risk Assessment of Welded Offshore Steel Pipelines
Steel structures continuously exposed to offshore marine environments are prone to corrosion. This can be of major economic and perhaps of environmental significance. The risk of these scenarios occurring can be assessed using good quality data, good quality corrosion and pitting models and structural reliability assessment. Recently, improved models for the prediction of longer term corrosion ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Research of the National Bureau of Standards
سال: 1937
ISSN: 0091-0635
DOI: 10.6028/jres.018.045