Kinetics of the Bainite Transformation in Austempered Ductile Iron ADI
نویسندگان
چکیده
منابع مشابه
The Bainite Reaction Kinetics in Austempered Ductile Iron
Bainitic reaction kinetics in ductile iron contained according to Ukrainian standard (weight %) 3.603.80 carbon, 2.60-2.80 Si, 0.12 Mn, 0.60 Cu and additionally alloyed by Mo (0.15-0.20) has been studied. It was found that the overall transformation kinetics becomes slower as transformation temperature increase. This is because more intensive redistribution of carbon into austenite at higher te...
متن کاملNear-Net-Shape Manufacturing of Austempered Ductile Iron (ADI) Components
Near Net Shape (NNS) manufacturing produces the engineering components closer to its final specification in single stage or minimum number of stages. ADI process technology is one of the NNS manufacturing technologies, currently being followed by the industries for manufacturing of engineering components at competitive price. Austempered Ductile Iron is a new class of engineering material which...
متن کاملKinetics of the bainite transformation
A theory is developed for the evolution of bainite as a function of time, temperature, chemical composition and austenite grain size. The model takes into account the details of the mechanism of transformation, including the fact that nucleation begins at the austenite grain surfaces, and that the growth of a sheaf occurs by the repeated nucleation of small platelets. Predictions made using the...
متن کاملEffects of Carbides on Fatigue Characteristics of Austempered Ductile Iron
Crack initiation and growth behaviour of an austempered ductile iron (ADI) austenitised at 800C and austempered at 260C has been assessed under three point bend fatigue conditions. Initiation sites have been identified as carbides remaining from the as cast ductile iron due to insufficient austenisation. The number of carbides cracking on loading to stresses greater than 275 MPa is critical in ...
متن کاملDevelopment of High Silicon Dual Phase Austempered Ductile Iron
This work deals with the feasibility of obtaining Austempered Ductile Iron with Dual Phase structures (DPADI) through heat treatment, starting from different as-cast microstructures. The mechanical properties on these microstructures were evaluated. DPADI microstructures were obtained by adding different tenors of silicon (2.4% to 4.2%) to the melts and keeping the other alloying elements const...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advances in Materials Science
سال: 2016
ISSN: 2083-4799
DOI: 10.1515/adms-2016-0008