Kinetics of corrosion-driven cathodic disbondment on organic coated trivalent chromium metal-oxide-carbide coatings on steel
نویسندگان
چکیده
منابع مشابه
Electrochemical Impedance Spectroscopy as a Method to Predict Delamination of Coated Steel in Cathodic Disbondment Tests
A study was undertaken using electrochemical impedance spectroscopy to measure delamination and compare that measurement, which can be performed on the sample repeatedly, with the accepted method of cathodic disbondment (CD) testing, the major drawback of which is that this measurement can only be done once on the sample; in reaching this goal, EIS could be used to predict delamination based on...
متن کاملPlasma spraying and characterization of chromium carbide – nickel chromium coatings
Chromium carbide – nickel chromium powder Cr3C2-25wt.NiCr was plasma sprayed by a water-stabilized system WSP®. A series of experiments with variable feeding distance was carried out. Basic characterization of coatings was done by XRD, SEM and light microscopy plus image analysis. Microhardness was measured on polished cross sections. The main focus of investigation was on resistances against w...
متن کاملAn Electrochemical Measurement for Evaluating the Cathodic Disbondment of Buried Pipeline Coatings under Cathodic Protection
Steel pipelines are susceptible to corrosion by the action of corrosive substance in the environment and one of the most common failure modes in buried pipeline coatingis cathodic disbondment. Consequently, Electrochemical Impedance Spectroscopy (EIS) was used to assess the effect of three important parameters, the thickness of coating, the artificial defect ...
متن کاملCut-edge corrosion study on Al-rich metallic coated steel
Aluminium additions to metallic coatings on steel substrates have been accepted as a successful solution versus the standard zinc based coatings. The development of these products responds to the market’s demand of more versatile products, which faces the leaching effect of zinc and the rising cost of obtaining this element, among the main advantages. However, these materials show a special sen...
متن کاملan electrochemical measurement for evaluating the cathodic disbondment of buried pipeline coatings under cathodic protection
steel pipelines are susceptible to corrosion by the action of corrosive substance in the environment and one of the most common failure modes in buried pipeline coatingis cathodic disbondment. consequently, electrochemical impedance spectroscopy (eis) was used to assess the effect of three important parameters, the thickness of coating, the artificial defect and electrolyte type, on cathodic di...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Corrosion Science
سال: 2019
ISSN: 0010-938X
DOI: 10.1016/j.corsci.2019.04.037