Mechanical behaviour of TWIP steel under shear loading
Twinning induced plasticity steels (TWIP) are very good candidate for automotive industry applications because they potentially offer large energy absorption before failure due to their exceptional strain hardening capability and high strength. However, their behaviour is drastically influenced by the loading conditions. In this work, the mechanical behaviour of a TWIP steel sheet sample was in...
متن کاملTwin-Induced Plasticity of an ECAP-Processed TWIP Steel
The TWIP steels show high strain hardening rates with high ductility which results in high ultimate tensile strength. This makes their processing by equal channel angular pressing very difficult. Up to now, this has only been achieved at warm temperatures (above 200 C). In this paper, a FeMnCAl TWIP steel has been processed at room temperature and the resulted microstructure and mechanical prop...
متن کاملObservation of Stacking Fault Tetrahedral in TWIP Steel
Low stacking fault energy face centered cubic (FCC) materials contain characteristic defect structures. Stacking fault tetrahedral are one of those rare structures that occur under special experimental conditions. For the first time, stacking fault tetrahedral were observed in Fe-30Mn-3Al-3Si twinning induced plasticity (TWIP) steel. Their presence resulted from a quenching heat treatment.
متن کاملTWIP-effect and thermo-mechanical treatment of a stable high-manganese austenitic stainless steel
Austenitic carbon steels that exhibit excellent mechanical properties due to the twinning-induced plasticity effect have been studied extensively. On the other hand, austenitic stainless steels usually achieve good strength and ductility via transformation-induced plasticity. However, relying on martensite transformation for strength may cause problems such as delayed cracking. Therefore, the t...
متن کاملEqual Channel Angular Pressing of a TWIP steel: Microstructure and mechanical response
A Fe-20.1Mn-1.23Si-1.72Al-0.5C TWIP steel with ultra-fine grain structure was successfully processed through Equal Channel Angular Pressing (ECAP) at warm temperature up to four passes following the BC route. The microstructure evolution was characterized by Electron Back Scattered Diffraction (EBSD) to obtain the grain maps, which revealed an obvious reduction of grain size, as well as a decre...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Structural Integrity
سال: 2017
ISSN: 2452-3216
DOI: 10.1016/j.prostr.2017.07.154