Isothermal Sections of Al-Ni-Zr Ternary System at 850 and 1050 °C
نویسندگان
چکیده
منابع مشابه
Precipitation evolution in Al–Zr and Al–Zr–Ti alloys during isothermal aging at 375–425 C
Formation of Al3Zr or Al3(Zr1 x Tix) precipitates with a metastable L12 structure was investigated in conventionally solidified A1–0.1 Zr, Al–0.2 Zr, Al–0.1 Zr–0.1 Ti, and Al–0.2 Zr–0.2 Ti (at.%) alloys aged isothermally at 375, 400, or 425 C. Pronounced hardening results from nanometer-scale, spheroidal Al3Zr or Al3(Zr1 xTix) (L12) precipitates within solute-enriched dendrites. Interdendritic ...
متن کاملPrecipitation evolution in Al–Zr and Al–Zr–Ti alloys during aging at 450–600 C
The transformation of Al3Zr (L12) and Al3(Zr1 xTix) (L12) precipitates to their respective equilibrium D023 structures is investigated in conventionally solidified Al–0.1Zr and Al–0.1Zr–0.1Ti (at.%) alloys aged isothermally at 500 C or aged isochronally in the range 300– 600 C. Titanium additions delay neither coarsening of the metastable L12 precipitates nor their transformation to the D023 st...
متن کاملSupercooled melting in multicomponent Zr–Al–Cu–Ni diffusion couples
Diffusion couples combining a hcp Zr90Al10 supersaturated solid solution with a fcc Cu64Ni36 solid solution were annealed at 410 °C for different times. The reaction at the interface was investigated by transmission electron microscopy and energy dispersive x-ray spectroscopy. The investigations show the formation of a noncrystalline layer at the interface between the two solid solutions that g...
متن کاملRadial flow in central Al+Al and Ni+Ni reactions at 2 AGeV
The question whether a global freeze-out occurs in heavy-ion collisions below and up to energies of a few AGeV and to which extent this phenomenon is embedded into a collective radial expansion has been studied by various experiments [1, 2, 3]. Measurements performed at BEVALAC [1] indicate that the emission of light particles (p, d, t, He, α) around mid-rapidity in Au+Au collisions at 1 AGeV i...
متن کاملGlass Forming Ability and Corrosion Resistance of Zr-Cu-Ni-Al-Ag Bulk Metallic Glass
Zr70−xCu12.5Ni10Al7.5Agx (x = 0–10) bulk metallic glasses (BMGs) have been prepared by copper mold casting. The glass-forming ability (GFA) and corrosion behavior of Zr-based BMGs have been investigated. It is found that the GFA of Zr-based BMGs first increases and then decreases with the increase of the Ag content, and the best glass former is Zr65Cu12.5Ni10Al7.5Ag5 with the maximum thickness ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Phase Equilibria and Diffusion
سال: 2013
ISSN: 1547-7037,1863-7345
DOI: 10.1007/s11669-013-0248-8