Isothermal Age-Hardening Behaviour in Commercial Dental Gold Alloys containing Palladium
نویسندگان
چکیده
منابع مشابه
Isothermal age-hardening behaviour in commercial dental gold alloys containing palladium.
The isothermal age-hardening behaviour in the commercial dental gold alloys containing palladium was studied by means of resistometric, hardness, X-ray and electron microscopy. Drastic overageing occurred following prolonged ageing. The mechanism of the overageing was interpreted as a loss of coherency at the interfaces of the adjacent lamellae which consists of the equilibrium AuCu I ordered p...
متن کاملEffect of age hardening on corrosion resistance and hardness of CoCrMo alloys used in dental engineering
Purpose: The goal of the study is to research the effect of various time of ageing on corrosion resistance, hardness and structures of Remanium 2000+ Co-Cr-Mo alloys used in prosthodontia. Design/methodology/approach: To investigation was prepared mould, cast in 1430°C and realized the heat treatment: solutioning in 1250°C by 3 hours and then ageing in 850°C by 4, 8, 16 and 24 hours. Electroche...
متن کاملThe Strain Hardening Behaviour of Supersaturated Al-Cu Alloys
Julien da Costa Teixeira, Yves Bréchet , Yuri Estrin and Christopher Hutchinson ARC Centre of Excellence for Design in Light Metals, Department of Materials Engineering, Monash University, Clayton, VIC, 3800, Australia Institut Jean Lamour, Dépt SI2M, Ecole des Mines, Parc de Saurupt, 54042 Nancy, France SIMAP, Institut Nationale Polytechnique de Grenoble, St. Matin D’Hères, 38000, France CSIRO...
متن کاملPrecipitation hardening in a dental low-gold alloy.
Age-hardening characteristics in a dental low-gold alloy composed of 40.0 wt% Au-35.0 wt% Ag-7.9 wt% Pd-7.0 wt% Cu-5.0 wt% In-3.5 wt% Zn-1.5 wt% Sn, were investigated by means of the hardness test, XRD study, SEM observations and EPMA. The following results were obtained. The age-hardening was characterized by a precipitation of Cu-rich alpha2 phase in the a phase. The softening that occurred f...
متن کاملHigh-strength age hardening copper–titanium alloys: redivivus
In this review the decomposition of supersaturated Cu–Ti solid solutions and subsequent microstructural evolution are discussed in terms of modern views of precipitation from solid solution. This update is motivated by an anticipated emergence of these alloys as technologically significant high-strength, high-conductivity, precipitation hardened alloys over the next decade replacing conventiona...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Dental Materials Journal
سال: 1984
ISSN: 1881-1361,0287-4547
DOI: 10.4012/dmj.3.253