Isochronal Annealing Behaviors of Magnesium Alloy AZ31 After Hot Deformation

THE DEFORMATION BEHAVIOR OF AZ31 MAGNESIUM ALLOY AT ELEVATED TEMPERATURES

AZ31 magnesium alloy is considered as a promising alloy in various applications and industries. Furthermore, to design a proper hot working process (rolling, forging and extrusion), the assessment of hot working behaviour of the alloy is necessary. Accordingly, the hot deformation behaviour of AZ31 alloy was studied through hot compression testing method This was carried out in a wide range of ...

Hot Deformation Mechanisms in AZ31 Magnesium Alloy Extruded at Different Temperatures: Impact of Texture

The hot deformation characteristics of AZ31 magnesium alloy rod extruded at temperatures of 300 °C, 350 °C and 450 °C have been studied in compression. The extruded material had a fiber texture with > < 0 1 10 parallel to the extrusion axis. When extruded at 450 °C, the texture was less intense and the > < 0 1 10 direction moved away from the extrusion axis. The processing maps for the material...

Mechanisms of Plastic Deformation in AZ31 Magnesium Alloy Investigated by Acoustic Emission and Electron Microscopy

Anodizing of Magnesium Alloy Az31 by Alkaline Solution

-Anodizing of AZ 31 Mg alloy was investigate in 3M KOH solution for 10, 20 and 30min. at constant voltage of 5V. Atomic force microscope (AFM) used to investigate the roughness of anodic film formed on the surface while the scanning electron microscope (SEM) was used to determine the morphology of the anodic film, it was found that the roughness of the anodic film is mainly depend on the anodiz...

A comparative study on constitutive modeling of hot deformation flow curves in AZ91 magnesium alloy

Modeling the flow curves of materials at elevated temperatures is the first step in mathematical simulation of the hot deformation processes of them. In this work a comparative study was provided to examine the capability of three different constitutive equations in modeling the hot deformation flow curves of AZ91 magnesium alloy. For this, the Arrhenius equation with strain dependent constants...