Irradiation Induced Localized Amorphization in Mo-Re Alloy Films
نویسندگان
چکیده
منابع مشابه
Irradiation Induced Localized Amorphization in Mo-Re Alloy Films
To investigate the irradiation properties of Mo-Re alloy of low Re content (atm%: 0% 8:4%), Mo-Re alloy films were irradiated by 200 keV xenon ions at the dose of 5 10 ions/cm. Different irradiation effects were observed on the samples of different Re content. While the sample of pure Mo remained the same after irradiation, obvious localized amorphization phenomenon took place in the sample wit...
متن کاملIrradiation-induced defect clustering and amorphization in silicon carbide
Previous computer simulations of multiple 10 keV Si cascades in 3C–SiC demonstrated that many damage-state properties exhibit relatively smooth, but noticeably different, dose dependencies. A more recent analysis of these damage-state properties, which includes additional data at low and intermediate doses, reveals more complex relationships between system energy, swelling, energy per defect, r...
متن کاملDeformation-induced localized solid-state amorphization in nanocrystalline nickel
Although amorphous structures have been widely obtained in various multi-component metallic alloys, amorphization in pure metals has seldom been observed and remains a long-standing scientific curiosity and technological interest. Here we present experimental evidence of localized solid-state amorphization in bulk nanocrystalline nickel introduced by quasi-static compression at room temperature...
متن کاملCompositional Dependent Amorphization in Zr Alloy Films by Means of Ni-Implantation
Ni-implantation has been conducted for sputter deposited Zr alloy films to investigate compositional dependent amorphization behavior in proportion to Ni in Zr alloys. As-deposited Zr and Zr–Cu with thickness of 200 nm shows columnar hcp-Zr and nano-crystalline hcp-Zr(Cu), respectively. Implantation of 150 keV Niþ with the amount of 1 10 ions/cm induces amorphization of Zr and Zr(Cu) with 100 n...
متن کاملMo-Si-B Alloy Development
Alloys consisting of the phases α-Mo (Mo solid solution), Mo3Si, and Mo5SiB2 (“T2”) were fabricated by ingot and powder metallurgy. A novel powder-metallurgical processing technique was developed which allows the fabrication of silicide alloys with a continuous α-Mo matrix. In these alloys the relatively ductile and tough α-Mo matrix acts as a “binder” for brittle silicide particles. An alloy p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2010
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.m2009306