Irradiation Assisted Stress Corrosion Cracking (IASCC)

Effects of irradiation on intergranular stress corrosion cracking

Intergranular stress corrosion cracking &YSCC) is a pervasive and generic problem in current light water reactor and advanced reactor designs that can lead to widespread component failure. IASCC is believed to be due to either to changes in the grain boundary composition, the microstructure or the water chemistry and corrosion potential. Of greatest interest are the changes in composition and m...

Stress Corrosion Cracking

Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking

Finite element analyses were conducted to clarify the role of corrosion product films (CPFs) in stress corrosion cracking (SCC). Flat and U-shaped edge-notched specimens were investigated in terms of the CPF-induced stress in the metallic substrate and the stress in the CPF. For a U-shaped edge-notched specimen, the stress field in front of the notch tip is affected by the Young's modulus of th...

Tarnish Resistance, Corrosion and Stress Corrosion Cracking of Gold Alloys

Tarnishing, corrosion and stress corrosion cracking (SeC) of gold alloys are related phenomena. They present problems when they occur in gold jewellery, dental gold alloys and electronic devices. They are exploited, however, in the depletion gilding and finishing of gold jewellery; and in the extraction, refining and fire assaying of gold. There is still much that is not known about these pheno...

ARPA Coupling Program on Stress - Corrosion Cracking

A progress report of the ret arch invest carried out on the problem of stress-cor high strength materials under ARPA Order Work at Carnegie-Mellon University, Lehi Georgia Institute of Technology, The Boe American University, and the Naval Resea cerning test techniques, materials chara metallurgy, surface studies, and corrosi described. The report is divided into t covering work on high strengt...