Investigation on Micro-Hardness, Surface Roughness and SEM of Nano TiO2/B4C/Graphene Reinforced AA 7075 Composites Fabricated by Frictional Stir Processing

نویسندگان

چکیده

The current work seeks to discover and choose the proper friction stir processing (FSP) settings for aluminum alloy 7075 surface composites enhanced by adding three unique nanoparticles of titanium dioxide (TiO2), B4C, graphene superior performance. FSP is only method that produces higher amounts particle distribution nanoscale reinforcing. For sample fabrication, a special relatively high rotational speed 2000 rpm feed rate 45 mm/min were tested with suitable range parameters (800–2000 rpm, 25–45 mm/min). To measure micro-hardness roughness different nano composites, they studied under various conditions. findings showed produced at speeds 1400 decreased granule distributions 39% 73%, respectively, increased 54%. According microstructure investigations, good bonding was between AA7075 substrate generated 1200 base metal processed specimens 800 rpm. AA7075/B4C composite rotating had than other two composites.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Tribological behaviour of AA 5083/Micron and Nano SiC composites fabricated by ultrasonic assisted stir casting process

Metal Matrix composites (MMCs) are light weight, high-strength materials with potential application in areas such as automobile, aerospace, defence and other industries. MMCs are projected to significantly reduce the overall weight of the vehicle and aircraft while maintaining satisfactory structural strength. Micron and Nano-sized ceramic particle reinforced aluminum matrix composites fabricat...

متن کامل

Effect of Tip Shape of Frictional Stir Burnishing Tool on Processed Layer’s Hardness, Residual Stress and Surface Roughness

Friction stir burnishing (FSB) is a surface-enhancement method used after machining, without the need for an additional device. The FSB process is applied on a machine that uses rotation tools (e.g., machining center or multi-tasking machine). Therefore, the FSB process can be applied immediately after the cutting process using the same machine tool. Here, we apply the FSB to the shaft material...

متن کامل

On the PEEK composites reinforced by surface-modified nano-silica

The nano-sized silica fillers reinforced poly(ether ether ketone) (PEEK) composites were fabricated by means of compression molding technique. he nano-sized silica, measuring 30 nm in size, was firstly modified by surface pretreatment with stearic acid. The performances and properties f the resulting PEEK/SiO2 nanocomposites were examined in terms of tensile loading, hardness, dynamic mechanica...

متن کامل

MICROSTRUCTURE, HARDNESS AND SURFACE ROUGHNESS CHARACTERIZATION OF EBM FABRICATED Ti-6Al-4V SAMPLES

Electron beam melting (EBM) is among the modern additive manufacturing processes whereby metal powders are selectively melted to produce very complicated components with superior mechanical properties. In this study, microstructure, hardness, and surface roughness of EBM fabricated Ti6Al4V samples were characterized. The results showed that the microstructure consisted of epitaxially-grown prim...

متن کامل

Analysis of Surface Roughness and Micro-hardness in Roller Burnishing of Aluminum Alloy 6061

Burnishing is a chip-less finishing process, in which a hard roller or ball presses the surface layer of part to perform plastic deformation in the surface layer and produce improved finish, enhanced hardness and compressive residual stresses on the surface of special materials such as Aluminum and Brass. In the following research, the effect of input parameters such as feed rate, cutting speed...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Crystals

سال: 2023

ISSN: ['2073-4352']

DOI: https://doi.org/10.3390/cryst13030522