Interlaminar Shear Strength of Medium-Density Fiberboard (MDF) Measured by Three-Point Short-Beam Shear Test and Comparison with that Obtained by Asymmetric Four-Point Bending Test
نویسندگان
چکیده
منابع مشابه
Medium Density Fiberboard (mdf) Manufacturing
In this study wheat straw was taken from Ankara province. In order to produce dry process MDF, urea formaldehyde resin was used at the ratio of 8 %, 10 % and 12 %, 1 % ammonium chloride was used as hardening agent on the basis of dry fiber weight. On the other hand, 5, 6 and 7 min. pressing times were applied. Alcohol benzene, cold water, hot water and 1 % NaOH solubility of wheat straw were 5....
متن کاملComparison of shear bond strength of the stainless steel metallic brackets bonded by three bonding systems
Introduction: In orthodontic treatment, it is essential to establish a satisfactory bond between enamel and bracket. After the self-etch primers (SEPs) were introduced for the facilitation of bracket bonding in comparison to the conventional etch-and-bond system, multiple studies have been carried out on their shear bond strengths which have yielded different results. This study was aimed at co...
متن کاملHot-pressing process modeling for medium density fiberboard (MDF)
In this paper we present a numerical solution for the mathematical modeling of the hot-pressing process applied to medium density fiberboard. The model is based in the work of Humphrey [1982], Humphrey and Bolton [1989] and Carvalho and Costa [1998], with some modifications and extensions in order to take into account mainly the convective effects on the phase change term and also a conservativ...
متن کاملShort-Beam Three-Point Bend Tests in Syntactic Foams. Part II: Effect of Microballoons Content on Shear Strength
Epoxy binders containing microballoons ranging from 38.5 to 57.7% by volume were cast in a mold and cured, and the resulting slabs were sectioned to yield short-beam test coupons. The strength changes with microballoons content were noted. These reveal an increase from 3.87 to 5.79 MPa for a decrease in microballoons content from 57.7 to 38.5%. Mechanical data were correlated with fractographic...
متن کاملFlexural Properties and Fracture Behavior of Nanoporous Alumina film by Three-Point Bending Test
This study investigated the influence of porosity on the flexural property of a nanoporous alumina film. When the porosity of the alumina film increased, both bending strength and modulus declined. The results from the bending test revealed that the setting of the film during the bending test had significant influence on the flexural property. Fracture only occurred when the porous side of the ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 2013
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.79.105