Interlaminar Fracture of Stitched GFRP Laminates
نویسندگان
چکیده
منابع مشابه
Mode I Interlaminar Fracture Toughness of Natural Fiber Stitched Flax/Epoxy Composite Laminates – Experimental and Numerical Analysis
The mode I interlaminar fracture toughness of stitched and unstitched composite laminates of continuous UD flax fiber and epoxy matrix was experimentally and numerically investigated. A twistless flax fiber yarn was used for stitching purpose. The mode I interlaminar energy release rate of the unstitched and stitched laminates was experimentally determined through Double Cantilever Beam (DCB) t...
متن کاملFracture Behaviour of Polyetherimide (PEI) and Interlaminar Fracture of CF/PEI Laminates at Elevated Temperatures
(2005) Fracture behavior of polyetherimide (PEI) and interlaminar fracture of CF/PEI laminates at elevated temperatures. Abstract To investigate effects of environmental temperature on fracture behaviour of a polyetherimide (PEI) thermoplastic polymer and its carbon fibre (CF/PEI) composite, experimental and numerical studies were performed on compact tension (CT) and double cantilever beam (DC...
متن کاملPerformance of Corrosion-Damaged HSC Beams Strengthened with GFRP Laminates
This paper presents the results of an experimental program conducted for evaluating the performance of corrosion damaged HSC beams strengthened with GFRP laminates. Five Beam specimens of size 150x250x3000 mm were caste and tested for the present investigation. One beam specimen was neither corroded nor strengthened to serve as reference. Two beams were corroded to serve as corroded control. A ...
متن کاملInterlaminar Mode II Fracture Characterization
Delamination is an important concern in the context of structural behaviour of laminated composite materials. It is known that delamination can diminish the stiffness and the strength of the material and promote structural failure. Delamination onset and growth is governed by interlaminar fracture toughness of the material. Delamination propagation is frequently dominated by mode II fracture; c...
متن کاملImprovement of the mode II interface fracture toughness of glass fiber reinforced plastics/aluminum laminates through vapor grown carbon fiber interleaves
The effects of acid treatment, vapor grown carbon fiber (VGCF) interlayer and the angle, i.e., 0° and 90°, between the rolling stripes of an aluminum (Al) plate and the fiber direction of glass fiber reinforced plastics (GFRP) on the mode II interlaminar mechanical properties of GFRP/Al laminates were investigated. The experimental results of an end notched flexure test demonstrate that the aci...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advanced Composites Letters
سال: 1996
ISSN: 2633-366X,2633-366X
DOI: 10.1177/096369359600500101