Interlaminar crack propagation in MWCNT/fiber reinforced hybrid composites
نویسندگان
چکیده
منابع مشابه
Modeling dynamic crack propagation in fiber reinforced composites including frictional effects
Dynamic crack propagation in a unidirectional carbon/epoxy composite is studied through finite element analyses of asymmetric impact (shear loading) of a rod against a rectangular plate. A finite deformation anisotropic visco-plastic model is used to describe the constitutive response of the composite. Crack propagation is simulated by embedding zero thickness interface element along the crack ...
متن کاملShear crack formation and propagation in fiber reinforced cementitious composites (FRCC)
Knowledge of the mechanisms controlling crack formation, propagation and failure of FRCC under shear loading is currently limited. This paper presents a study that utilized photogrammetry to monitor the shear deformations of two FRCC materials and ordinary concrete (OC). Multiple shear cracks and strain hardening of both FRCC materials was observed under shear loading. The influence of fibers, ...
متن کاملFinite Element Modeling of Delamination Crack Propagation in Laminated Composites
Finite element analysis of the delamination crack propagation in laminated composites is presented. Fracture mechanics based Virtual Crack Closure Technique (VCCT), and the cohesive element technique, have been used to simulate the delamination initiation and propagation under Mode-I type loading. Detailed description of the parameter selection process for these two techniques with ABAQUS®/Stan...
متن کاملFracture and Fatigue Crack Propagation in Graded Composites
The propagation of cracks in graded materials under monotonic and cyclic loading was investigated via experiment and simulation. Graded alumina/epoxy composite specimens exhibiting a variation in composition from 5% to 65% epoxy, representing a twenty-fold variation in Young’s modulus, across a region of width between 6 and 20 mm, were produced by a multistep infiltration technique. Crack initi...
متن کاملFatigue-Crack Propagation Behavior of Ductile/Brittle Laminated Composites
A study has been made of the fatigue-crack propagation properties of a series of laminated Nbreinforced Nb3Al intermetallic-matrix composites with varying microstructural scale but nominally identical reinforcement volume fraction (20 pct Nb). It was found that resistance to fatigue-crack growth improved with increasing metallic layer thickness (in the range 50 to 250 mm) both in the crack-divi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Express Polymer Letters
سال: 2009
ISSN: 1788-618X
DOI: 10.3144/expresspolymlett.2009.19