Interfacial Segregation, Pore Formation, and Scale Adhesion on NiAl Alloys
نویسندگان
چکیده
منابع مشابه
Study of the Mechanism and Causes of Pore Formation in Sr-modified Al-Si Alloys
The formation of microporosity in modified Al-Si alloys has been reviewed in the present study. A major concern in modification is the increased tendency to form microporosity in the macro-shrinkage free Al-Si alloy castings. It has also been demonstrated that at low hydrogen contents (0.1cc/ 100g, Al), where only shrinkage porosity should occur, the effect of Sr-modification on porosity conten...
متن کاملStudy of the Mechanism and Causes of Pore Formation in Sr-modified Al-Si Alloys
The formation of microporosity in modified Al-Si alloys has been reviewed in the present study. A major concern in modification is the increased tendency to form microporosity in the macro-shrinkage free Al-Si alloy castings. It has also been demonstrated that at low hydrogen contents (0.1cc/ 100g, Al), where only shrinkage porosity should occur, the effect of Sr-modification on porosity conten...
متن کاملsimulation and experimental studies for prediction mineral scale formation in oil field during mixing of injection and formation water
abstract: mineral scaling in oil and gas production equipment is one of the most important problem that occurs while water injection and it has been recognized to be a major operational problem. the incompatibility between injected and formation waters may result in inorganic scale precipitation in the equipment and reservoir and then reduction of oil production rate and water injection rate. ...
Point Defects in Nial Alloys under Pressure
We investigate the eeect of elevated pressures on the point defect ther-modynamics in NiAl alloys. A particular motivation for this study is due to the expected elimination of structural vacancies on the Al-rich side at high pressure. We employ the density functional theory to compute point defect energies as a function of pressure, which are in turn used as input to the Wagner-Schottky model. ...
متن کاملContinuum theory of interfacial segregation
Theoretical work in the field of interfacial segregation is mainly focused on the Gibbsian approach that uses the dividing surface construct. In this article a continuum approach to the problem of interfacial segregation in multicomponent hydrostatically compressed alloys is developed and the segregation at homophase and heterophase interfaces is considered on common grounds. The Gibbs adsorpti...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Oxidation of Metals
سال: 2005
ISSN: 0030-770X,1573-4889
DOI: 10.1007/s11085-005-1954-3