Interfacial Microstructures and Bonding Strength between Aluminum Nitride and Silver Brazing Filler Metals Containing Various Active Elements
نویسندگان
چکیده
منابع مشابه
Wettability of Brazing Filler Metals on Copper and Copper Alloys
The possibility of alloying can not be avoided at the interface between molten brazing filler metal and base metal in brazing, so the wettability of brazing filler metal can not be easily explained theoretically. We used the original apparatus for wettability test and investigated the relation between the wettability of brazing filler metals of Ag-P-Cu and Ag-Cu-Zn-Cd systems on copper and the ...
متن کاملInterfacial Structure Analysis on Direct Bonding Metals to Plastics†
This research investigated the direct bonding mechanism of dissimilar materials such as metals and plastic by the conventional hot pressing process. The press area of 4 x 4 mm2 was used for direct bonding. The results of the study showed that titanium was completely bonded to polyamide 66. On the other hand, titanium was not bonded to polystyrene. In the case of bonding material of titanium wit...
متن کاملCharging effect of aluminum nitride thin films containing Al nanocrystals.
In this work, the Al-rich AIN thin film is deposited on Si substrate by radio frequency (RF) sputtering to form a metal-insulator-semiconductor (MIS) structure. Al nanocrystals (nc-Al) are formed and embedded in the AIN thin film. Charge trapping/detrapping in the nc-Al leads to a shift in the flat-band voltage (VFB) of the MIS structure. The charge storage ability of the AIN thin films contain...
متن کاملبررسی خواص مکانیکی اتصالات در لحیم کاری سخت آلیاژ V4-Al6-Ti به آلیاژ 410 SS در شرایط خلا
In this research, Ti-6Al-4V alloy was brazed with 410 stainless steel by three different filler metals as silver-base, nickel-base, and titanium-base alloys. In order to obtain optimum clearance, brazing was done in three different clearances of 0.02, 0.04 and 0.06 mm. Also, the strength and hardness of the brazing zone were investigated. The results of shear strength showed that the brazed ...
متن کاملThe Microstructural Evolution of Vacuum Brazed 1Cr18Ni9Ti Using Various Filler Metals
The microstructures and weldability of a brazed joint of 1Cr18Ni9Ti austenitic stainless steel with BNi-2, BNi82CrSiBFe and BMn50NiCuCrCo filler metals in vacuum were investigated. It can be observed that an interdiffusion region existed between the filler metal and the base metal for the brazed joint of Ni-based filler metals. The width of the interdiffusion region was about 10 μm, and the mic...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2004
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.112.305