Interface behavior of tungsten coating on stainless steel by electro spark deposition

Effect of Deposition Regime on Tribological Behavior of VK8Coating on 1.2344 Tool Steel Obtained by Electro Spark Method

In this study, the effect of deposition regime on the wear behavior of VK8 coating applied to 1.2344 tool steel by electro spark method (ESA) was investigated. After sample preparation, the coating with high and low regime was applied. To assess the wear behavior, the pin on disk test method according to ASTM G99-04, was used. For surveying surface morphology and cross section of the coating as...

Growth Defects and Chromium Content Loss during the Deposition of Stainless Steel by CAE-PVD and Its Effect on the Corrosion and Passivation Behavior of the Coating

In the present study, the effects of growth defects and chromium content loss on the degradation of corrosion and passivation of cathodic arc evaporation (CAE-PVD) of stainless steel coating were investigated in 2 M sulphuric acid solution. EDS analysis indicated that the micro-particles were obtained during the coating growth. In addition, it was detected that the growth defects had poor adhes...

Factors Affecting Friction Coating on Stainless Steel 304

Low carbon steels are widely used for structural applications because of its ease in fabrication and the moderate strength it posses. However, its pure corrosion resistance at normal atmosphere is a matter of serious concern.

Interface Deepening of Novel Tungsten Carbide- Stainless Steel Composites through Hr-tem

growth defects and chromium content loss during the deposition of stainless steel by cae-pvd and its effect on the corrosion and passivation behavior of the coating

in the present study, the effects of growth defects and chromium content loss on the degradation of corrosion andpassivation of cathodic arc evaporation (cae-pvd) of stainless steel coating were investigated in 2 m sulphuricacid solution. eds analysis indicated that the micro-particles were obtained during the coating growth. in addition,it was detected that the growth defects had poor adhesion...