Initial stage of degradation process of alumina-silica refractory by molten Al-5Mg alloy
نویسندگان
چکیده
Initial stages of the refractory degradation process by molten Al-5Mg alloy were investigated analyzing structures caused an interaction with metal during heat cycles. The aggregate, found to be poly-crystalline, consisting cristobalite (SiO2) and mullite (Al6Si2O13), was deteriorated ahead surrounding matrix. Metal permeated into refractory, forming a thin layer along crucible surface below line at early stage process, which would later serve as bases for infiltration path through above line. A discontinuous film (thickness<3μm), most likely MgAl2O4, formed “melt / refractory” interface. At experimental temperature 1150°C, Mg in build up gas MgAl2O4 film/refractory interface easily diffuse aggregate body react components SiO2 Al6Si2O13 form Al-Mg-Si-O compounds. This followed while reducing compound MgAl2O4. Through initial finally successive chain reactions, resulting deterioration crucible.
منابع مشابه
INFLUENCE OF NANO SILICA ON PROPERTIES AND MICROSTRUCTURE OF HIGH ALUMINA ULTRA-LOW CEMENT REFRACTORY CASTABLES
Colloidal silica bonded refractory castables have been developed recently. It was found that colloidal silica is one of the best binders can substitute other binders such as cement in No Cement Castable (NCC) and Ultra Low Cement Castable (ULCC) refractories. Also composition of colloidal silica with appropriate additives resulted in a gel form which makes the initial strength. Moreover, the na...
متن کاملCorrosion Behavior of Al-2wt%Cu Alloy Processed By Accumulative Roll Bonding (ARB) Process
Accumulative roll bonding (ARB) imposes severe plastic strain on materials without changing the specimen dimensions. ARB process is mostly appropriate for practical applications because it can be performed readily by the conventional rolling process. An Al-2wt%Cu alloy was subjected to ARB process up to a strain of 4.8. Stacking of materials and conventional roll-bonding are repeated in the pro...
متن کاملthe effect of keeping reflective journals by language instructors on the process of reading comprehension among iranian high school students
خواندن ودرک مطلب از مهمترین مهارتها در یادگیری زبان خارجی محسوب می شود. این تحقیق تاثیر برگه های تامل برانگیز هدایت شده را در ارتقاع مهارت خواندن ودر ک مطلب در دانش اموزان دبیرستانی ایرانی بررسی می نماید. ازمجموع ?2 دانش آموز سال چهارم دبیرستان شهید رجایی شهرستان اسلامشهر¸ پس از اجرای آزمون استاندارد ((nelson 150a تعداد 39 دانش آموز که نمرات آنها یک سطح انحراف معیار بالاتر یا پایین تر ازمعدل قر...
control of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 2022
ISSN: ['0451-5994', '1880-8018']
DOI: https://doi.org/10.2464/jilm.72.631