Influence of welding current intensity on susceptibility to intergranular corrosion in welded joints of stainless steel
نویسندگان
چکیده
منابع مشابه
Determination of susceptibility to intergranular corrosion and electrochemical reactivation behaviour of AISI 316L type stainless steel
In this study, double loop electrochemical potentiokinetic reactivation (DLEPR) test was applied to determine the degree of sensitization in 316L type stainless steel, where obtained results were correlated with revealed microstructures after oxalic acid test and weight loss measurements of Streicher and Huey acid tests. Best agreement was provided with test parameters which are 1 M H2SO4 and 0...
متن کاملInfluence of multiple welding cycles on microstructure and corrosion resistance of a super duplex stainless steel
.......................................................................................... v Appended Publications .................................................................. vii Table of
متن کاملEffect of Different Welding Parameters on the Mechanical and Microstructural Properties of Stainless Steel 304H Welded Joints
In this research work, an attempt has been made to examine the different welding parameters which affect the weldability of 304H Austenitic stainless steel (ASS) welded joint using the proper filler wire. Chemical composition of filler wire was same as that of base metal. Further this study addressed the combined effect of various welding parameters on the metallurgical and mechanical propertie...
متن کاملInfluence of Laser Ablation on Stainless Steel Corrosion Behaviour
Laser ablation is the method for material removing from a surface using pulsed lasers. It is used for surface structuring, laser drilling or laser marking. A change of the corrosion behavior of a base material caused by thermal effects during laser processing is an important problem of this technology. Possibilities of surface modification of stainless steel using laser ablation are presented i...
متن کاملAttachment of Listeria monocytogenes to an austenitic stainless steel after welding and accelerated corrosion treatments.
Austenitic stainless steels, widely used in food processing, undergo microstructural changes during welding, resulting in three distinctive zones: weld metal, heat-affected zone, and base metal. This research was conducted to determine the attachment of Listeria monocytogenes in these three zones before and after exposure to a corrosive environment. All experiments were done with tungsten inert...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Zavarivanje i zavarene konstrukcije
سال: 2017
ISSN: 0354-7965
DOI: 10.5937/zzk1704149j