Influence of the Cooling Rate on Mechanical and Corrosion Properties of Ferritic Si–Mo Ductile Cast Iron
نویسندگان
چکیده
Abstract In this study, the effect of cooling rate controlled by different castings thickness ranging from 3 to 25 mm on mechanical and corrosion behavior Si–Mo ductile iron (DI) was investigated. SEM-EBSD investigations demonstrated that nodule counts, nodularity, ferrite phase increased while ferritic grain size decreased with decreasing in casting wall thickness; turn led improvements tensile properties DI. The DI investigated after immersion times a 3.5 wt pct NaCl solution via electrochemical experiments. results showed resistance following order: > 5 13 mm. indicated all tested samples exhibited galvanic between nobler carbide matrix phases. SEM analysis dissolution pearlite exposed accumulated DI’s surface, which intense acceleration. higher rates were observed for those thicknesses could be associated contents pearlite/carbide.
منابع مشابه
Damage Analysis of a Ferritic SiMo Ductile Cast Iron Submitted to Tension and Compression Loadings in Temperature
Tensile and compression tests were carried out on a ductile cast iron for temperatures up to 1073 K. The damage caused inside and around graphite nodules was evaluated as a function of the local equivalent plastic strain by using microstructural quantifications. The mechanical properties are strongly dependent on a temperature above 773 K. Concerning tensile behavior, an evolutional law issued ...
متن کاملInfluence of 1 wt-% addition of Ni on structural and mechanical properties of ferritic ductile irons
To cite this version: Lacaze, Jacques and Larrañaga, Peio and Asenjo, Iker and Suarez, Ramon and Sertucha, Jon Influence of 1 wt-% addition of Ni on structural and mechanical properties of ferritic ductile irons. (2012) Materials Science and Technology, Vol. 28 (n° 5). pp. 603-608. ISSN 0267-0836 Open Archive Toulouse Archive Ouverte (OATAO) OATAO is an open access repository that collects the ...
متن کاملdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولEffect of Alloying Elements on the Microstructure and Mechanical Properties of Austempered Ductile Iron Alloys
متن کامل
: the effect of sericin levels (silk glue protein) on rate of in vitro maturation, fertilization and culture of sheep oocytes
هدف از آزمایش اول بررسی اثر سطوح مختلف سریسین [0 (control), 0.1, 0.5, 1.0, 2.5 %] افزوده شده به محیط , ivm بر cumulus cell expansion، بلوغ هسته و توسعه متوالی جنین، در گوسفندان نژاد سنجابی در فصل تولید مثلی می باشد. از سرگیری میوز به وسیله خارج شدن اولین پولار بادی اندازه گیری و هم چنین درصد رسیدن جنین های دو سلولی به مرحله کلیواژ و بلاستوسیت نیز به عنوان نشانه ای از میزان شایستگی توسعه اولیه ج...
ذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metallurgical and Materials Transactions
سال: 2023
ISSN: ['1073-5623', '1543-1940']
DOI: https://doi.org/10.1007/s11661-023-07023-x