Influence of spark plasma sintering temperature on the densification, microstructure and mechanical properties of Al-4.5 wt.%Cu alloy
نویسندگان
چکیده
منابع مشابه
Influence of Rolling Temperature on Microstructure and Mechanical Properties of Cryorolled Al-Mg-Si Alloy
An effect of rolling temperature on the mechanical properties and microstructural evolution of an Al-Mg-Si alloy was studied. The material was rolled up to a true strain of ∼0.7 at three different temperatures viz; room temperature, liquid propanol and liquid nitrogen. The liquid nitrogen rolled sample exhibited superior properties with a yield and tensile strength of 332 MPa and 364 MPa, respe...
متن کاملSpark Plasma Sintering of Commercial Zirconium Carbide Powders: Densification Behavior and Mechanical Properties
Commercial zirconium carbide (ZrC) powder is consolidated by Spark Plasma Sintering (SPS). Processing temperatures range from 1650 to 2100 °C. Specimens with various density levels are obtained when performing single-die SPS at different temperatures. Besides the single-die tooling setup, a double-die tooling setup is employed to largely increase the actual applied pressure to achieve higher de...
متن کاملSpark Plasma Sintering of a Gas Atomized Al7075 Alloy: Microstructure and Properties
The powder of an Al7075 alloy was prepared by gas atomization. A combination of cellular, columnar, and equiaxed dendritic-like morphology was observed in individual powder particles with continuous layers of intermetallic phases along boundaries. The cells are separated predominantly by high-angle boundaries, the areas with dendritic-like morphology usually have a similar crystallographic orie...
متن کاملFull densification of Molybdenum powders using Spark Plasma Sintering
Pure molybdenum powder was sintered using Spark Plasma Sintering under various temperatures, and holding times, under a pressure of 77 MPa and a heating rate at 700°C/min. After sintering, a carbide layer was observed at the surface. The carbide layer thickness, the relative density of the sample as well as the microhardness and the grain size of Mo were measured. The carbide thickness depends ...
متن کاملInfluence of Li2Sb Additions on Microstructure and Mechanical Properties of Al-20Mg2Si Alloy
It is found that Li2Sb compound can act as the nucleus of primary Mg2Si during solidification, by which the particle size of primary Mg2Si decreased from ~300 to ~15–25 μm. Owing to the synergistic effect of the Li2Sb nucleus and adsorption-poisoning of Li atoms, the effect of complex modification of Li-Sb on primary Mg2Si was better than that of single modification of Li or Sb. When Li-Sb cont...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Metallurgica Sinica (English Letters)
سال: 2013
ISSN: 1006-7191,2194-1289
DOI: 10.1007/s40195-013-0159-z