Influence of semisolid heat treatment on aging behavior of Al- Cu alloy
نویسندگان
چکیده
منابع مشابه
Aging behavior in Cu–Al–Be shape memory alloy
This article reports positron annihilation spectroscopy and calorimetric measurements of the aging behavior in a Cu–Al–Be shape memory alloy. An excess of single vacancies is retained in the alloy as a result of a quench. All vacancies in excess disappear after long aging time, and a migration energy EM51.060.1 eV for this process has been found to be larger than in other Cu-based shape memory ...
متن کاملInfluence of Natural Aging Time on Two-Step Aging Behavior of Al-Mg-Si(-Cu) Alloys
Nanoclusters formed during natural aging cause the negative effect of the two-step aging in the age-hardenable Al-Mg-Si alloys. The relationship between the clustering behavior during natural aging and the two-step aging behavior was studied using the hardness, differential scanning calorimetry (DSC), electrical resistivity measurements, transmission electron microscopy (TEM) observation in the...
متن کاملTHE INFLUENCE OF DRY SLIDING ON PRCIPITATION HARDENING BEHAVIORS OF Al-Cu-Si ALLOY
Abstract: Cold working performed before an aging treatment has a significant effect on size and amount of precipitate produced. This could be caused by the increase in defect density, such as vacancies and dislocations. In this research, the Al-Cu-Si alloy was solution-treated, wear-tested and then artificially aged for a period of 1–5 h. Changes in the amount of precipitate, in the lattice par...
متن کاملEFFECTS OF Al-5TI-1B MASTER ALLOY AND HEAT TREATMENT ON THE MICROSTRUCTURE AND DRY SLIDING WEAR BEHAVIOR OF AN Al-12Zn-3Mg-2.5Cu ALLOY
In this study the effect of Al–5Ti–1B grain refiner on the structural characteristics and wear properties of Al–12Zn–3Mg–2.5Cu alloy was investigated. The optimum amount for Ti containing grain refiners was selected as 2 wt.%. T6 heat treatment, (i.e. heating at 460 °C for 1 h before water quenching to room temperature and then aging at 120 °C for 24 h) was applied for all specimens before wear...
متن کاملThe Influence of Heat Treatment and High Energy Ball Milling on the Density, Hardness, and Wear Behavior of Al 7150 Alloy via Hot Uniaxial Compaction
The effect of the milling time & ageing on the hardness, density, and wear characteristics of Al 7150 alloy specimens made via powder metallurgy has been studied. The different constituents of Al 7150 alloy were processed in a planetary ball milling set up with a BPR of 10:1 for 5 hours, 10 hours, and 20 hours. At 400 °C, the milled powders were subsequently hot compacted in a punch die setup. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOP Conference Series: Materials Science and Engineering
سال: 2015
ISSN: 1757-899X
DOI: 10.1088/1757-899x/75/1/012019