Influence of Precursor Preparation via Ammonolysis Route on Alumina-Zirconia Nanostructure.
نویسندگان
چکیده
منابع مشابه
Preparation Zirconia Toughened Alumina by Deflocculation-Flocculation Route (TECHNICAL NOTE).
Partially stabilized zirconia (PSZ) agglomerate toughened alumina has been prepared by the "deflocculation-flocculation" technique, using 2 and 3 mol. % Y2O3-doped zirconia powders. Samples containing up to about 30 vol.% zirconia were obtained. The resulting microstructure seems to be mainly influenced by the physical properties of the starting powders, e.g. agglomerate size and the specific s...
متن کاملInfluence of heat treatment on synthesis of stoichiometric perovskite PbTiO3 nanostructure via hydrothermal method
In this research, the stoichiometric perovskite lead titanate (PbTiO3) nanostructurewas synthesized successfully by the hydrothermal method. The effect of heattreatment of the autoclave and the furnace on the structure of this materialwas investigated. Titanium dioxide (TiO2), titanium tetrachloride (TiCl4) and leadoxide (PbO), lead nitrate (Pb(NO3)2) were used as the ti...
متن کاملCrack growth resistance of alumina, zirconia and zirconia toughened alumina ceramics for joint prostheses.
Mono-phase bio-ceramics (alumina and zirconia) are widely used as femoral heads in total hip replacements (THR) as an alternative to metal devices. Unfortunately, the orthopaedic community reports significant in-vivo failures. Material scientists are already familiar with composites like alumina zirconia. Since both are biocompatible, this could prove to be a new approach to implants. This pape...
متن کاملInfluence of nano alumina coating on the flexural bond strength between zirconia and resin cement
PURPOSE The purpose of this in vitro study is to examine the effects of a nano-structured alumina coating on the adhesion between resin cements and zirconia ceramics using a four-point bending test. MATERIALS AND METHODS 100 pairs of zirconium bar specimens were prepared with dimensions of 25 mm × 2 mm × 5 mm and cementation surfaces of 5 mm × 2 mm. The samples were divided into 5 groups of 2...
متن کاملDetection of tetragonal zirconia in alumina–zirconia powders by thermoluminescence
The thermoluminescence (TL) after excitation by UV or X-rays radiation of alumina-zirconia powders is investigated. The composites present five of the characteristic peaks of zirconia at −170, −145, −90, 0 and 95 °C. After a thermal treatment of mixed oxides, a new peak is observed at −35 °C in TL. This peak reveals the presence of stabilized tetragonal zirconia in the material. Moreover by com...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2001
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.109.1267_201